WNM360 Description

This standard applies to the quenched and tempered wear-resistant steel plate series with the steel plate thickness not greater than 100mm, and is mainly used for structural steel plates used in the processing and manufacturing of wear-resistant and vulnerable parts for mines and various construction machinery.

China Grade: WNM360

Enterprise Standard: WYJ030-2010

Application: Thickness ≤100mm quenching and tempering wear-resistant steel plate

Composition: manufacturer, purpose, hardness and quality grade

Kategori: Etiket:
WNM360 Aşınmaya Dayanıklı Çelik Levha
WNM360 Aşınmaya Dayanıklı Çelik Levha

WNM360(NM360) grade is a high-grade quenched and tempered wear-resistant steel plate produced by WuSteel; its grade is low than WNM400 Ve NM400.

This standard applies to the quenched and tempered wear-resistant steel plate series with the steel plate thickness not greater than 100mm, and is mainly used for structural steel plates used in the processing and manufacturing of wear-resistant and vulnerable parts for mines and various construction machinery.

China Grade: WNM360

Enterprise Standard: WYJ030-2010

Application: Thickness ≤100mm quenching and tempering wear-resistant steel plate

Composition: manufacturer, purpose, hardness and quality grade

It belongs to the quenched and tempered wear-resistant steel plate produced by Wugang, which implements the enterprise standard WYJ030-2010.
How to express the grade: The grade of steel plate is composed of four parts representing the manufacturer, use, hardness and quality grade in order, for example:
WNM360A, WNM360B, WNM360L, etc.
Symbol: W—represents the first letter of the Chinese pinyin of “Wu” of WuSteel;
NM—the first letter of the Chinese pinyin of the characters “Nai” and “Mo” for wear resistance;
A and B–respectively the quality level, meanwhile, A represents that the steel plate is not impacted, and B represents that the steel plate is impacted at 20 degrees normal temperature;
L–means high weldability steel plate (guarantee wear resistance, reduce carbon equivalent, improve weldability)
The steel plate adopts straight edge rolling, the head and tail are cut, and the two longitudinal sides are not cut, and the trimming margin is controlled according to the normal trimming plate.
The remaining size, shape, weight and allowable deviation of the steel plate shall comply with GB/T709.
The chemical composition (melting analysis) of WNM360 meets the requirements of the following table:
Seviye
C
Ve
Mn
P
S
Ay
CR
İçinde
B
A
≤0,22
≤0,60
≤1,60
≤0,025
≤0,015
≤0,50
≤1,00
/
≤0,004
B
≤0,22
≤0,60
≤1,60
≤0,025
≤0,015
≤0,50
≤1,00
≤0,60
≤0,004
Note: It is permissible to add microalloy strengthening elements, such as Nb, V, Ti, etc. to the steel plate.
Smelting method: electric furnace + refining outside the furnace.
Delivery status: quenching + tempering = quenching and tempering.
The mechanical properties meet the requirements of the following table:
Seviye
Hardness (HBW)
20°CAKV longitudinal J
A
320~400
supply
B
320~400
≥21
The surface quality of the steel plate meets the requirements of GB3274.
Serial number
Test items
Number of samples
Sampling method
Experiment method
1
Uzatmak
1
GB/T2975-82
GB228/T-2002
2
Şok
3
GB/T2975-82
GB/T229-1994
3
Bending test
1
GB/T2975-82
GB/T232
4
sertlik
1
GB/T2975-82
GB231-84
Brinell hardness (HBW) inspection, according to the national standard GB/T231, the surface of the steel plate is milled off 1.0-2.2 mm, and then the hardness is tested on this surface.