Creusabro® 8000: a high performance wear and impact resistant steel
Creusabro® 8000 is a high performance wear resistant steel, exhibiting a wear resistance 50% higher than conventional 500HB water quenched steel, combined with excellent weldability and very acceptable workability.
Rather than relying exclusively on a high hardness level, properties of Creusabro® 8000 are improved as a result of the combination of an enriched alloying content (chromium, nickel, molybdenum and titanium) and specific heat treatment procedures.
The moderate hardness of Creusabro® 8000 in the as delivered condition makes processing operations like cutting, machining and forming easier and far better than ordinary water quenched steels.
When in service, Creusabro® 8000 strongly improves its wear resistance by a surface hardening effect of about +70 HB under the action of local plastic deformations caused by impact with rocks or pressure by the abrasive particles.
Creusabro® 8000 is ideal for applications in mines and quarries, cement and steelmaking industries, public works and agricultural machinery. In the toughest industries such as mining and earth moving, the higher resistance to wear and impact abrasion translates into increased service life of wearparts and components made of Creusabro® 8000 against conventional water quenched steels. As a result, significant costs saving benefits are achieved to plant maintenance budgets.
The grade is suitable for all types of abrasion, sliding or impact, dry or wet environments, including operating temperatures up to 350-450°C.
Advantages
- Geçmek® Benzersiz, en iyi, Kanıtlanmış
A high performance wear and impact resistant steel. Creusabro® 8000 is a high performance wear resistant steel, exhibiting a wear resistance 50% higher than conventional 500HB water quenched steel, combined with excellent weldability and very acceptable workability. Rather than relying exclusively on a high hardness level, properties of Creusabro® 8000 are improved as a result of the combination of an enriched alloying content (chromium, nickel and molybdenum) and specific heat treatment procedures such as oil quenching. - Değirmen imalat uygulamasında kullanılan kontrollü söndürme oranlarına sahip özel konsept:
– develop a bainite-martensite mixed microstructure with retained austenite absorbing impact
– stimulate a fine dispersion of hard micro-alloyed carbides delaying cracking and surface peel off
– Yerel plastik deformasyonların etkisi altında +70 HB'lik yüzey sertleştirme etkisi sayesinde hizmetteki aşınma direnci büyük ölçüde iyileştirilir. Bu, TRIP etkisi olarak bilinir. - +P'den 0'e kadar daha uzun servis ömrü
– Creusabro® 8000 outlast by 50 -100% classical 500HB, 550HB-class plates …
Alternatif olarak Creusabro® çelikleri, standart suyla söndürülmüş plakalarla aynı aşınma ömrü için önemli ölçüde ağırlık tasarrufu ve artırılmış taşıma kapasitesi potansiyeli (daha düşük kalınlık gereklidir) sunar. - Bir aşınma plakası içindeki yapısal kapasite Creusabro® -20°C'de minimum 32 J garantili darbe enerjisine sahiptir. Sadece aşınma astarı olarak değil, potansiyel olarak yapısal bir malzeme olarak da performans göstermek için gerekli olan sağlamlığı ve kaynaklanabilirliği sunar.
- Atölye dostu,
– yumuşak söndürme işlemi sayesinde plaka içinde artık gerilim yoktur, dolayısıyla kesme sırasında ve sonrasında deformasyon olmaz
– excellent flatness < 5 mm/m achieved without cold-deformation
– teslimat durumunda daha yumuşak malzeme, aşınma direncinden ödün vermeden atölyede karmaşık parçaların düzgün ve kolay işlenmesini kolaylaştırır. - Isı ve aşınma direnci
Spesifik kimyasal bileşim ve başlangıç mikro yapısı, 250°C'nin üzerinde sertliğini kaybeden geleneksel su ile söndürülmüş ürünlerle karşılaştırıldığında yumuşamaya karşı yüksek bir direnç sağlar.
– in-service temperature up to 450°C
– Isıdan Etkilenen Bölge azaltıldı, örn. alevle kesme veya kaynaklama sonrasında
– gerekirse Creusabro plakaları başka bir ısıl işleme gerek kalmadan sıcak şekillendirilebilir.
DS-WRS-CREUSABRO8000-07-2020