C62400
Product description: Aluminum bronze 11%
Tempers: HR50 drawn and stress relieved
Solids: 1/2″ to 3″ O.D.*
Standart uzunluklar: 144″
*Diğer boyutlar için değirmene danışın
Tipik kullanımlar
Fasteners: nuts
Industrial: bushings, cams, drift pins, gears, hydraulic bushings, support bushings, tie rods, valve balls, wear plates, welding wire
Introduction to C62400 alloy:
C62400 aluminum bronze alloy belongs to the aluminum bronze series and is mainly composed of copper (Cu), aluminum (Al), lead (Pb) and other elements. The addition of aluminum can increase the strength, hardness and corrosion resistance of the alloy, while the addition of lead can improve the lubrication properties of the alloy. C62400 alloy has high strength and hardness, as well as good corrosion resistance and wear properties.
C62400 performance features:
– Mechanical properties: C62400 alloy has high tensile strength, yield strength and elongation.
C62400 aluminum bronze alloy is a common copper alloy with good mechanical properties, corrosion resistance and wear properties. It is widely used in the fields of shipbuilding, marine engineering, chemical equipment and automobile industry. It has good processing performance and can be formed by cold working and hot working. Heat treatment can further increase the strength and hardness of the alloy.
Benzer veya eşdeğer spesifikasyon
| CDA | ASTM | SAE | AMS | Federal | Askeri | Diğer |
|---|---|---|---|---|---|---|
| C62400 | B150 B150M | J461 J463 |
Kimyasal bileşim
| %Cu1 | Sn% | Fe% | Al% | Mn% | Ve% | ||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
Chemical composition according to ASTM B150/B150M-19 1Cu value includes Ag. Not: Cu + adı geçen elementlerin toplamı, �,5 min. Tek değerler maksimumları temsil eder. | |||||||||||
| Rem. | 00,20 | 2.00- 4.50 | 10.00- 11.50 | 00,30 | 00,25 | ||||||
İşlenebilirlik
| Bakır alaşımı UNS No. | İşlenebilirlik derecesi | Yoğunluk (lb/inç3 68 °F'de) |
|---|---|---|
| C62400 | 50 | 00,269 |
Mekanik özellikler
C62400
HR50 drawn and stress relieved Temper
Size range: 1/2″ and under rod
| Çekme mukavemeti, min | Akma mukavemeti, yük altında %0,5 uzamada, min | Elongation, in 4x Diameter or Specimen Thickness, min | Rockwell “B” sertliği | Notlar | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | minimumdan maksimuma HRB | |
| 95 | 655 | 45 | 310 | 10 | ||
Size range: over 1/2″ to 1″ rod inclusive
| Çekme mukavemeti, min | Akma mukavemeti, yük altında %0,5 uzamada, min | Elongation, in 4x Diameter or Specimen Thickness, min | Rockwell “B” sertliği | Notlar | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | minimumdan maksimuma HRB | |
| 95 | 655 | 45 | 310 | 12 | ||
Size range: over 1″ to 2″ rod inclusive
| Çekme mukavemeti, min | Akma mukavemeti, yük altında %0,5 uzamada, min | Elongation, in 4x Diameter or Specimen Thickness, min | Rockwell “B” sertliği | Notlar | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | minimumdan maksimuma HRB | |
| 90 | 620 | 43 | 295 | 12 | ||
Size range: over 2″ to 3″ rod inclusive
| Çekme mukavemeti, min | Akma mukavemeti, yük altında %0,5 uzamada, min | Elongation, in 4x Diameter or Specimen Thickness, min | Rockwell “B” sertliği | Notlar | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | minimumdan maksimuma HRB | |
| 90 | 620 | 40 | 275 | 12 | ||
Fiziki ozellikleri
CDA tarafından sağlanan fiziksel özellikler | |||||||||||
| ABD Geleneği | Metrik | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Erime noktası – sıvı | 1900 °F | 1038°C | |||||||||
| Erime noktası – katılaşma | 1880 °F | 1027 °C | |||||||||
| Yoğunluk | 00,269 lb/inç3 68 °F'de | 7,45 gr/cm3 20 °C'de | |||||||||
| Spesifik yer çekimi | 7.45 | 7.45 | |||||||||
| Elektiriksel iletkenlik | 12% IACS at 68 °F | 0.07 MegaSiemens/cm at 20 °C | |||||||||
| Termal iletkenlik | 34 Btu/sq ft/ft hr/°F at 68 °F | 59 W/m at 20 °C | |||||||||
| Termal genleşme katsayısı 68-572 | 9 · 10-6 °F (68-572 °F) başına | 15.6 · 10-6 °C başına (20-300 °C) | |||||||||
| Özgül ısı kapasitesi | 068 °F'de 0,09 Btu/lb/°F | 20 °C'de 377,1 J/kg | |||||||||
| Gerilmede esneklik modülü | 17000 ksi | 117212MPa | |||||||||
| Sertlik modülü | 6400 ksi | 44127 MPa | |||||||||
İmalat özellikleri
CDA tarafından sağlanan üretim özellikleri | |||||||||||
| Teknik | Uygunluk | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Lehimleme | Tavsiye edilmez | ||||||||||
| Lehimleme | Adil | ||||||||||
| Oksiasetilen kaynağı | Tavsiye edilmez | ||||||||||
| Gaz korumalı ark kaynağı | İyi | ||||||||||
| Kaplamalı metal ark kaynağı | İyi | ||||||||||
| Nokta kaynağı | İyi | ||||||||||
| Dikiş kaynağı | İyi | ||||||||||
| Alın kaynağı | İyi | ||||||||||
| Soğuk çalışılma kapasitesi | Fakir | ||||||||||
| Sıcak şekillendirilme kapasitesi | Harika | ||||||||||
| Dövülebilirlik Derecesi | 80 | ||||||||||
| İşlenebilirlik derecesi | 50 | ||||||||||
Termal özellikler
CDA tarafından sağlanan termal özellikler *Sıcaklık Fahrenheit cinsinden ölçülür. | |||||||||||
| Tedavi | Minimum* | Maksimum* | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Tavlama | 1100 | 1200 | |||||||||
| Sıcak tedavi | 1400 | 1625 | |||||||||
Ortak imalat süreçleri
Hot bending, hot forging
CDA tarafından sağlanan ortak imalat süreçleri