C67410 Manganese Bronze Alloy
Much like other manganese bronze alloys, C67410 resists corrosion well. When used in bearings, C67410 can handle high speeds and heavy loads. By including manganese, iron, and aluminum, this alloy resists seizing.
C67410 has high strength for use in heavy-load applications. Some typical uses include:
- Manganese Bronze Bushings
- Manganese Bronze Cams
- Manganese Bronze Connecting Rods
- Manganese Bronze Cylinder Liners
- Manganese Bronze Gears
- Manganese Bronze Hydraulic Piston Shoes
- Manganese Bronze Shafts
- Manganese Bronze Valve Guides & Chain Guides
- Manganese Bronze Wear Plates
C67410 Introduction
Copper alloys are extremely popular as they have strong corrosion resistance to many types of substances and environments. They are resistant to fresh water, steam, marine and industrial atmospheres, non-oxidizing minerals, caustic solutions, organic acids, moist ammonia, halogens, soils, and sulfides.
Copper alloys, however, have poor resistance to inorganic acids. The following datasheet discusses the chemical composition and properties of copper UNS C67410.
องค์ประกอบทางเคมี
The chemical composition of copper UNS C67410 is given in the following table.
| ธาตุ | เนื้อหา (%) |
|---|---|
| ทองแดง ลูกบาศ์ก | 55.5 – 59 |
| นิเกิล, นิ | 2 |
| อะลูมิเนียม อัล | 1.3 – 2.3 |
| แมงกานีส, Mn | 1.0 – 2.4 |
| เหล็ก, เฟ | 1 |
| ลีด, พีบี | 0.8 |
| ซิลิกอนใช่ | 0.7 – 1.3 |
| Tin, Sn | 0.5 |
| สังกะสี, สังกะสี | สมดุล |
คุณสมบัติทางกล
The mechanical properties of copper UNS C67410 are tabulated below.
| คุณสมบัติ | เมตริก | อิมพีเรียล |
|---|---|---|
| แรงดึง | 483-750 MPa | 70 -109 ksi |
| ความแข็งแรงของผลผลิต | 234-430 MPa | 34 – 62 ksi |
| การยืดตัว | 28-10% | 28-10% |
| Hardness, Brinell | 140-200 | 140-200 |
(measured at room temperature, 68 F (20 C)
| อารมณ์โกรธ | Section ขนาด | เย็น Work | Typ/ นาที | อุณหภูมิ | แรงดึง ความแข็งแกร่ง | ผลผลิต ความแข็งแกร่ง (0.5% ext. under load) | ผลผลิต ความแข็งแกร่ง (0.2% offset) | ผลผลิต ความแข็งแกร่ง (0.05% offset) | El | ร็อคเวลล์ ความแข็ง | Vickens Hard. | บริเนล Hard. | เฉือน ความแข็งแกร่ง | Fatigue Strength* | Izod ผลกระทบ ความแข็งแกร่ง | ||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ใน. | % | F | ksi | ksi | ksi | ksi | % | บี | ค | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb | ||
| mm. | ค | MPa | MPa | MPa | MPa | MPa | MPa | เจ | |||||||||||
| ร็อด | |||||||||||||||||||
| O60 | 0.75 | 0 | TYP | 68 | 70 | 34 | – | – | 28 | 78 | – | – | – | – | – | – | – | – | 0.0 |
| 19 | 20 | 483 | 234 | – | – | 28 | 78 | – | – | – | – | – | – | – | – | 0.0 | |||
| บาร์ | |||||||||||||||||||
| M30 | 0.0 | 0 | TYP | 68 | 78 | 38 | – | – | 26 | 78 | – | – | – | – | – | – | – | – | 0.0 |
| 0.0 | 20 | 538 | 262 | – | – | 26 | 78 | – | – | – | – | – | – | – | – | 0.0 | |||
| ร็อด | |||||||||||||||||||
| HR02 | 0.75 | 0 | TYP | 68 | 92 | 55 | – | – | 20 | 87 | – | – | – | – | – | – | 48 | 29 | 0.0 |
| 19 | 20 | 634 | 379 | – | – | 20 | 87 | – | – | – | – | – | – | 331 | 200 | 0.0 | |||
| บาร์ | |||||||||||||||||||
| HR02 | 0.0 | 0 | TYP | 68 | 85 | 45 | – | – | 24 | 83 | – | – | – | – | – | – | – | – | 0.0 |
| 0.0 | 20 | 586 | 310 | – | – | 24 | 83 | – | – | – | – | – | – | – | – | 0.0 | |||
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
Other Designations
Other designations that are equivalent to copper UNS C67410 include:
- SAE J461
- SAE J463
แอปพลิเคชั่น
Copper UNS C67410 finds application in:
- Cams
- เกียร์
- เพลา
- บูช
- Wear plates
- Cylinder liners
- Connecting rods
- Food conveyor chain
- Hydraulic piston shoes
- Valve guides and chain guides