Dillimax 690 Wear Resistant Steel Plate

DILLIMAX 690 Wear Resistant Steel Plate

DILLIMAX 690 is a high strength quenched and tempered, fine grained structural steel with a minimum yield strength of 690 MPa (100 ksi)²⁾ in its delivery condition (referring to the lowest thickness range).
Its mechanical properties are achieved by water quenching followed by tempering.
DILLIMAX 690 is preferentially used for welded steel structures within mechanical constructions, plant constructions and structural steel works, such as machines for structural engineering, conveying plants, hoists, cranes, flood gates, bridges and frameworks.

Product description

Designation and range of application

DILLIMAX 690 can be delivered in three qualities:

• Basic (B) with minimum impact values down to -20 °C (-4 °F)²⁾ : DILLIMAX 690 B
  Steel number 1.8931 – S690Q according to EN 10025-6
• Tough (T) with minimum impact values down to -40 °C (-40 °F)²⁾ : DILLIMAX 690 T
  Steel number 1.8928 – S690QL according to EN 10025-6
• Extra tough (E) with minimum impact values down to -60 °C (-76 °F)²⁾ : DILLIMAX 690 E
  Steel number 1.8988 – S690QL1 according to EN 10025-6, only up to a plate thickness of 200 mm

DILLIMAX 690 can be delivered as basic grade (B) or tough grade (T) in thicknesses from 6 to 250 mm (¼ to 10 in.)²⁾, as extra tough grade (E) in thicknesses from 6 to 200 mm (¼ to 8 in.)²⁾ according to the dimensional program.

Dimensions, which deviate from the usual dimensional program, may be possible on request.

DILLIMAX 690 fulfils the requirements of EN 10025-6.

DILLIMAX 690 Chemical composition

For the ladle analysis, the following limiting values in % are applicable :

The steel is fine grained through sufficient aluminium content.

The limiting CEV³⁾ values are lower than the values given in EN 10025-6 :

^a) The approximately converted values in brackets are for information only

Lower carbon equivalent values may be agreed on request.

¹⁾ The current version of this material data sheet can be also found on http://www.dillinger.de.
²⁾ The approximately converted values in brackets are for information only.
³⁾ CEV = C +Mn/6 +(Cr+Mo+V)/5 + (Cu+Ni)/15

DILLIMAX 690 Delivery condition

Water quenched and tempered according to EN 10025-6.

Mechanical and technological properties in the delivery condition

Tensile test at ambient temperature – transverse test pieces –

^a) The approximately converted values in brackets are for information only.
^b) If not apparent, the yield strength R_p0.2 is measured instead.
^c) These values apply if tested according to ASTM A370.
^d) Higher minimum values may be agreed on request. For Offshore applications special grades are available.

DILLIMAX 690 Impact test on Charpy-V-specimens

^a) The approximately converted values in brackets are for information only.
^b) The extra tough grade E according to this data sheet is only available up to a plate thickness of 200 mm. Enhanced impact energy requirements can be agreed upon request. For Offshore applications special grades are available.

The specified minimum value is the average of 3 tests. One individual value may be below the minimum average value specified, provided that it is not less than 70 % of that value. For plate thicknesses below 12 mm, the test can be carried out on Charpy-V test pieces with reduced width; the minimum width must be 5 mm. The minimum impact value will be decreased proportionally.

DILLIMAX 690 Testing

Tensile and impact tests will be performed according to EN 10025-6 once per heat and 40 t.

Tests on every heat treated plate may be possible on request. The test pieces are taken and prepared according to part 1 and 6 of EN 10025.

The tensile test is carried out on specimens of gauge length L_o = 5.65⋅√S_o respectively L_o = 5⋅d_o, in accordance with EN ISO 6892- 1. Tensile tests according to ASTM A370 may be agreed. The impact test will be carried out on Charpy-V-specimens in accordance with EN ISO 148-1 using a 2 mm striker. Unless otherwise agreed, the test will be performed at the lowest temperature of the corresponding quality on transverse test pieces.

Unless otherwise agreed, the test results are documented in an inspection certificate 3.1 in accordance with EN 10204.

Identification of plates

Unless otherwise agreed, the marking is carried out via steel stamps with at least the following information:

• steel grade (e.g. DILLIMAX 690 B, T or E)
• heat number
• number of mother plate and individual plate
• the manufacturer’s symbol
• authorized inspection representative’s sign

Processing

The entire processing and application techniques are of fundamental importance to the reliability of products made from this steel. The user should ensure that his design, construction and processing methods are aligned with the material, correspond to the state-of-the-art that the fabricator has to comply with and are suitable for the intended use. The customer is responsible for the selection of the material.

The recommendations of the EN 1011-2 (Welding) and CEN/TR 10347 (Forming) as well as recommendations regarding job safety in accordance with national rules should be observed.

DILLIMAX 690 Cold forming

Cold forming means forming below the maximum allowable stress relief temperature (560 °C/1040 °F)⁴⁾.

DILLIMAX 690 can be cold formed with regard to its high yield strength. Flame cut or sheared edges in the bending area should be ground before cold forming. Cold forming is related to a hardening of the steel and to a decrease in toughness. Some codes may limit the maximum permissible strain during cold forming.

Depending on the relevant code this can result in the need of larger bending radiuses than indicated in the chart. For larger cold forming amounts we recommend you to consult the steel producer prior to ordering.

During the processing, the necessary safety measures have to be taken, so that nobody will be exposed to a danger by a possible fracture of the work piece during the forming process.

The following geometries can usually be achieved by cold forming without the formation of surface defects (where t is the plate thickness):

DILLIMAX 690 Hot forming

If the temperature of 560 °C (1040 °F)⁴⁾ is exceeded, the initial tempering will be altered so that the mechanical properties are affected.

To regain the initial properties new quenching and tempering become necessary. However, water quenching of a formed workpiece or component will often be less effective than the original quenching in the plate mill so that the fabricator may not be able to reestablish the properties required and therefore hot forming may not be suitable.

In this respect we recommend you to contact the steel producer prior to ordering, in all cases where hot forming is required.

Finally, it is the fabricator’s responsibility to obtain the required values of the steel through an appropriate heat treatment.

DILLIMAX 690 Welding and flame cutting

Due to its high yield strength, DILLIMAX 690 requires special care during plate processing. For flame cutting, the following minimum preheating temperatures are recommended : 25 °C (77 °F)⁴⁾ for plate thickness up to 20 mm(0.8 in)⁴⁾, 50 °C (122 °F)⁴⁾ for plate thickness up to 50 mm (2 in)⁴⁾, 100 °C (212 °F)⁴⁾ for plate thickness up to 100 mm (4 in) ⁴⁾, 150 °C (302 °F)⁴⁾ for plate thickness up to 200 mm (8 in)⁴⁾ and 180 °C (356 °F)⁴⁾ for thicker plates.

For general welding instructions, please consult the EN 1011. In order to ensure that the tensile strength of the weld metal fulfils the requirements of the base metal, the heat input and interpass temperature must be limited during welding. Experience has shown that the welding conditions should be chosen so that the cooling time t8/5 does not exceed 20 seconds. This is applicable when using suitable filler materials of a corresponding yield strength class.

The high yield strength of the base material must be taken into account when choosing the filler materials.

It should be considered that increased heat input leads to lower tensile properties in the weld metal. If a stress relieving heat treatment is planned during or after plate processing, this must also be considered when selecting the filler materials. To avoid hydrogen-induced cold cracking, only filler materials, which add very little hydrogen to the base metal, may be used. Therefore, shielded arc welding should be preferred.

⁴⁾ The approximately converted values in brackets are for information only.

For manual arc welding, electrodes with basic coating (type HD<5 ml/100 g in accordance with ISO 3690), and dried according to the manufacturer’s instructions, should be used.

DILLIMAX 690 Heat treatment

If a stress relieving has to be considered because of constructional regulations, constructive reasons or because it is necessary for the fabrication, please consult us. The properties of structural components can be altered by a stress relief heat treatment.

Detailed instructions for flame cutting, welding, machining and about the structural properties of the DILLIMAX are provided in the technical information “MAKE SAVINGS WITH HIGH STRENGTH STEELS – DILLIMAX”.

General technical delivery requirements

Unless otherwise agreed, the general technical delivery requirements in accordance with EN 10021 apply.

Tolerances

Unless otherwise agreed, the tolerances will be in accordance with EN 10029, with class A for thickness and table 4, steel group H, for the maximum flatness deviation. Smaller flatness deviations may be possible on request prior to order.

Surface quality

Unless otherwise agreed, the specifications will be in accordance with EN 10163-2, class A2.

General note

If particular requirements are demanded and not covered in this data sheet, please contact us with the specifications for our review and agreement prior to ordering. The information in this data sheet is a product description.

Recommended: DILLIDUR IMPACT Wear Resistant Steel