C87850 Description
Copper silicon UNS C87850 has a copper content of not less than 74%.
Tabulated below are the mechanical properties of UNS C87850 permanent mold cast alloy as a function of heat treatment.
| 성질 | Elong. | 록웰 | |||
|---|---|---|---|---|---|
| NS | 씨 | NS | 30T | ||
| M05 | 21% | 74 | – | – | – |
| 16% | 70 | – | – | – | |
- C87850 Product description: Silicon brass
- Solids: Consult mill for sizes
- Tubes: Consult mill for sizes*
- Rectangles: Consult mill for sizes
- Standard lengths: 144″
- Shape/Form: Semi-finished, mill stock or near net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar
- Compliance: C87850 is compliant with key legislation including (1) Federal Safe Drinking Water Act – SDWA, (2) S. 3874 Federal Reduction of Lead in Drinking Water Act, (3) California AB1953, and (4) Vermont Act 193
*벽 두께는 공장에 문의하세요.
일반적인 용도
Industrial: valve bodies for water
Marine: marine products
Plumbing: faucets, plumbing fittings, water meter cases
유사하거나 동등한 사양
| CDA | 천식 | SAE | AMS | 연방 | 군대 | 다른 |
|---|---|---|---|---|---|---|
| C87850 | B505 B505M |
화학적 구성 요소
| Cu% | 납% | Sn% | 아연% | Fe% | 피% | % 1에서 | 백만% | Sb% | 그리고% | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 75.00- 78.00 | 0.02*- 0.09 | 0.30 | 렘. | 0.10 | 0.05- 0.20 | 0.20 | 0.10 | 0.10 | 2.70- 3.40 | ||
| Chemical composition according to ASTM B505/B505M-23*Pb content is greater than 0.02%. 1Ni value includes Co.Note: Cu + sum of named elements, 99.5% min. Single values represent maximums. | |||||||||||
가공성
| 구리합금 UNS No. | 가공성 등급 | Density (lb/in3 at 68 ˚F) |
|---|---|---|
| C87850 | 70 | 0.삼 |
기계적 성질
| 인장 강도, 최소 | Yield strength (at 0.5% extension under load,, min) | 신율(2인치 또는 50mm 최소) | 브리넬 경도(500kg 하중) | 비고 | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | minimum BHN | ||||||
| 65 | 448 | 25 | 172 | 8 | 103 | ||||||
| Mechanical properties according to ASTM B505/B505M-23 | |||||||||||
물리적 특성
| 미국 관습 | 미터법 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 녹는점 – 액체 | 1616 °F | 880 °C | |||||||||
| 녹는점 – 고상선 | 1571 °F | 855 °C | |||||||||
| 밀도 | 068°F에서 .3lb/in3 | 20°C에서 8.3gm/cm3 | |||||||||
| 전기 전도도 | 68°F에서 8% IACS | 0.046 MegaSiemens/cm at 20 °C | |||||||||
| 열 전도성 | 21.8 Btu/sq ft/ft hr/°F at 68 °F | 37.8 W/m at 20 °C | |||||||||
| Coefficient of thermal expansion 68-212 | 10.3 · 10-6 per °F (68-212 °F) | 17.8 · 10-6 per °C (20-100 °C) | |||||||||
| 열팽창 계수 68-392 | 10.3 · 10-6 per °F (68-392 °F) | 17.8 · 10-6 per °C (20-200 °C) | |||||||||
| 열팽창 계수 68-572 | 10.4 · 10-6 per °F (68-572 °F) | 18 · 10-6 per °C (20-300 °C) | |||||||||
| 비열용량 | 068°F에서 .09Btu/lb/°F | 20°C에서 377.1J/kg | |||||||||
| 인장 탄성 계수 | 15200 ksi | 104801 MPa | |||||||||
| CDA에서 제공하는 물리적 특성 | |||||||||||
제작 특성
| 기술 | 적당 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 납땜 | 훌륭한 | ||||||||||
| 브레이징 | 훌륭한 | ||||||||||
| 옥시아세틸렌 용접 | 좋은 | ||||||||||
| 스폿 용접 | 좋은 | ||||||||||
| 솔기 용접 | 좋은 | ||||||||||
| 맞대기 용접 | 좋은 | ||||||||||
| 냉간 가공 능력 | 가난한 | ||||||||||
| 열간 성형 능력 | 훌륭한 | ||||||||||
| 가공성 등급 | 70 | ||||||||||
| CDA에서 제공하는 제작 특성 | |||||||||||
열적 특성
| Thermal properties provided by CDATemperature is measured in fahrenheit. **For stress relief, Solution treatment and annealing – time is measured in hours/inch of thickness. For precipitation heat treatment – time is measured in hours. |