C69300 Lead Free Brass
C693 Lead-Free Brass has excellent dezincification corrosion resistance and excellent stress corrosion cracking resistance. One if its unique features is that it is corrosion resistant to chemicals found in water and gas. It has high strength equivalent to stainless steel. It also has good machinability, excellent hot forgeability, easily accepts solder and brazing, and has excellent polishing and plating capabilities. C69300 Lead-Free Brass is compliant with the Federal Drinking Water Act, and it also support applications following the U.S. EPA standards for antimicrobial performance.
Common Applications of C69300 Brass:
Plumbing
- Stop Valves
- PEX fittings
- Ball valves
- Commercial and Residential water faucet parts
자동차
- Fluid Connectors
- Sensor Bodies
- Thermostat Parts
산업
- Automatic Screw Machine Parts
- 볼트
- Condenser Tube Plate
- 견과류
- Pneumatic Fittings
- 펌프 부품
- Screw Machine Products
- 밸브 스템
- Valve Bodies for Water
C69300 Product description:
Compliance: C69300 is compliant with key legislation including (1) Federal Safe Drinking Water Act – SDWA, (2) S. 3874 Federal Reduction of Lead in Drinking Water Act, (3) California AB1953, (4) Vermont Act 193, and is NSF/ANSI/CAN 61-2022 compliant
일반적인 용도
Automotive: fluid connectors, sensor bodies, thermostat parts
Industrial: automatic screw machine parts, bolts, condenser tube plate, nuts, pneumatic fittings, pump parts, screw machine parts, valve bodies for water, valve stems
Marine: marine products, propeller shafts
Plumbing: faucet stems, faucets, plumbing fittings, water meter cases
유사하거나 동등한 사양
| CDA | 천식 | SAE | AMS | 연방 | 군대 | 다른 |
|---|---|---|---|---|---|---|
| C69300 | B371 B371M |
화학적 구성 요소
| Cu% 1 | 납% | Sn% | 아연% | Fe% | 피% | %2에서 | 백만% | 그리고% | |||
|---|---|---|---|---|---|---|---|---|---|---|---|
*Pb content is greater than 0.02%. 1Cu value includes Ag. 2Ni value includes Co. Single values represent maximums. | |||||||||||
| 73.00- 77.00 | 0.02*- 0.09 | 0.20 | 렘. | 0.10 | 0.04- 0.15 | 0.10 | 0.10 | 2.70- 3.40 | |||
가공성
| 구리합금 UNS No. | 가공성 등급 | 밀도(68°F에서 lb/in3) |
|---|---|---|
| C69300 | 85 | 0.300 |
기계적 성질
C69300
H02 하프 하드
Size range: up to 1/2″ inclusive
| 인장 강도, 최소 | 하중 하에서 0.5% 신장 시 항복 강도, 최소 | Elongation, 4x Diameter or Thickness of Specimen, min | 로크웰 "B" 경도 | 비고 | ||
|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | max HRB approx | |
| 85 | 585 | 45 | 310 | 5 | 85 | |
Size range: over 1/2″ to 1″ inclusive
| 인장 강도, 최소 | 하중 하에서 0.5% 신장 시 항복 강도, 최소 | Elongation, 4x Diameter or Thickness of Specimen, min | 로크웰 "B" 경도 | 비고 | ||
|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | max HRB approx | |
| 75 | 515 | 35 | 240 | 10 | 80 | |
Size range: over 1″ to 2 1/2″ inclusive
| 인장 강도, 최소 | Yield strength, at 00.5% extension under load,, min | Elongation, 4x Diameter or Thickness of Specimen, min | 로크웰 "B" 경도 | 비고 | ||
|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | max HRB approx | |
| 70 | 480 | 30 | 205 | 10 | 75 | |
물리적 특성
CDA에서 제공하는 물리적 특성 | |||||||||||
| 미국 관습 | 미터법 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 녹는점 – 액체 | 1616 °F | 880 °C | |||||||||
| 녹는점 – 고상선 | 1571 °F | 855 °C | |||||||||
| 밀도 | 068°F에서 .3lb/in3 | 20°C에서 8.3gm/cm3 | |||||||||
| 비중 | 8.3 | 8.3 | |||||||||
| 전기 전도도 | 68°F에서 8% IACS | 0.046 MegaSiemens/cm at 20 °C | |||||||||
| 열 전도성 | 21.8 Btu/sq ft/ft hr/°F at 68 °F | 37.76 W/m at 20 °C | |||||||||
| Coefficient of thermal expansion 68-212 | 10.3 · 10-6 per °F (68-212 °F) | 17.8 · 10-6 per °C (20-100 °C) | |||||||||
| 열팽창 계수 68-392 | 10.3 · 10-6 per °F (68-392 °F) | 17.8 · 10-6 per °C (20-200 °C) | |||||||||
| 열팽창 계수 68-572 | 10.4 · 10-6 per °F (68-572 °F) | 18 · 10-6 per °C (20-300 °C) | |||||||||
| 비열용량 | 068°F에서 .09Btu/lb/°F | 20°C에서 377.1J/kg | |||||||||
| 인장 탄성 계수 | 15200 ksi | 104801 MPa | |||||||||
제작 특성
CDA에서 제공하는 제작 특성 | |||||||||||
| 기술 | 적당 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 납땜 | 훌륭한 | ||||||||||
| 브레이징 | 좋은 | ||||||||||
| 옥시아세틸렌 용접 | 좋은 | ||||||||||
| 가스 차폐 아크 용접 | 좋은 | ||||||||||
| 코팅된 금속 아크 용접 | 좋은 | ||||||||||
| 스폿 용접 | 좋은 | ||||||||||
| 솔기 용접 | 좋은 | ||||||||||
| 맞대기 용접 | 좋은 | ||||||||||
| 냉간 가공 능력 | 가난한 | ||||||||||
| 열간 성형 능력 | 훌륭한 | ||||||||||
| 위조 가능성 등급 | 95 | ||||||||||
| 가공성 등급 | 85 | ||||||||||
열적 특성
CDA에서 제공하는 열적 특성 *온도는 화씨 단위로 측정됩니다. **For stress relief, solution treatment and annealing – time is measured in hours/inch of thickness. For precipitation heat treatment – time is measured in hours. | |||||||||||
| 치료 | 최저한의* | 최고* | Value* | Time** | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 스트레스 풀기 | 0 | ||||||||||
| 용액 처리 | 0 | ||||||||||
| 가열 냉각 | 932 | 1112 | |||||||||
| 뜨거운 치료 | 1202 | 1517 | |||||||||
일반적인 제조 공정
Forming and bending, machining, shearing
CDA에서 제공하는 일반적인 제조 프로세스