C67400 Description
- 가열 냉각
- UNS C67400 copper alloy is annealed between 427 and 593°C (800 and 1100°F).
- 냉간 가공
- UNS C67400 copper alloy has poor cold working capacity.
- 용접
- Welding processes suitable for UNS C67400 copper alloy include brazing, gas shielded arc welding, butt welding, spot welding, soldering and seam welding. Coated metal arc welding and oxyacetylene welding are not recommended for this alloy.
- 단조
- UNS C67400 copper alloy is forged between 593 and 677°C (1100 and 1250°F). The hot forgeability rating of this alloy is 100.
- 가공성
- The machinability rating of UNS C67400 copper alloy is 25.
- 열간 성형
- UNS C67400 copper alloy has excellent hot forming capacity.
- 애플리케이션
- UNS C67400 copper alloy can be used for pump components, heavy-duty mechanical components, valve stems and bearings.
C67400 Product description: Manganese bronze
UNS C67400 copper alloy is a hot forgeable alloy with good corrosion resistance and high strength. Applications include heavy duty mechanical components including bearings, valve stems and pump components.
The datasheet below provides an overview of UNS C67400 copper alloy.
일반적인 용도
Industrial: bushings, cams, chain guides, food conveyor chain, gears, shafts, wear plates
기타 : 커넥팅로드
유사하거나 동등한 사양
| CDA | 천식 | SAE | AMS | 연방 | 군대 | 다른 |
|---|---|---|---|---|---|---|
| C67400 | J461 J463 |
화학적 구성 요소
| Cu% | 납% | Sn% | 아연% | Fe% | % 1에서 | 알% | 백만% | 그리고% | |||
|---|---|---|---|---|---|---|---|---|---|---|---|
SAE J463에 따른 화학 성분 1Ni 값에는 Co가 포함됩니다. Single values represent maximums. | |||||||||||
| 57.00- 60.00 | 0.50 | 0.30 | 렘. | 0.35 | 0.25 | 0.50- 2.00 | 2.00- 3.50 | 0.50- 1.50 | |||
가공성
| 구리합금 UNS No. | 가공성 등급 | 밀도(68°F에서 lb/in3) |
|---|---|---|
| C67400 | 30 | 0.292 |
기계적 성질
SAE J463에 따른 기계적 성질
C67400
Extruded and drawn
크기 범위: 최대 1″ 포함
| 인장 강도, 최소 | Yield strength, at 00.5% extension under load,, min | Elongation, 4x Diameter or Thickness of Specimen, min | 로크웰 "B" 경도 | 비고 | ||
|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | 최소 HRB | |
| 78 | 540 | 40 | 275 | 8 | 84 | |
Size range: over 1″ to 2 ” inclusive
| 인장 강도, 최소 | Yield strength, at 00.5% extension under load,, min | Elongation, 4x Diameter or Thickness of Specimen, min | 로크웰 "B" 경도 | 비고 | ||
|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | 최소 HRB | |
| 75 | 515 | 40 | 275 | 10 | 80 | |
Size range: over 2″ to 3″ inclusive
| 인장 강도, 최소 | Yield strength, at 00.5% extension under load,, min | Elongation, 4x Diameter or Thickness of Specimen, min | 로크웰 "B" 경도 | 비고 | ||
|---|---|---|---|---|---|---|
| 크시 | MPa | 크시 | MPa | % | 최소 HRB | |
| 70 | 485 | 36 | 250 | 12 | 78 | |
물리적 특성
CDA에서 제공하는 물리적 특성 | |||||||||||
| 미국 관습 | 미터법 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 녹는점 – 액체 | 1625 °F | 885 °C | |||||||||
| 녹는점 – 고상선 | 1590 °F | 866 °C | |||||||||
| 밀도 | 0.292 lb/in3 at 68 °F | 8.08 gm/cm3 at 20 °C | |||||||||
| 비중 | 8.08 | 8.08 | |||||||||
| 전기 전도도 | 23% IACS at 68 °F | 020°C에서 .13 메가지멘스/cm | |||||||||
| 열 전도성 | 58 Btu/sq ft/ft hr/°F at 68 °F | 100.5 W/m at 20 °C | |||||||||
| 열팽창 계수 68-572 | 11 · 10-6 per °F (68-572 °F) | 19 · 10-6 per °C (20-300 °C) | |||||||||
| 비열용량 | 068°F에서 .09Btu/lb/°F | 20°C에서 377.1J/kg | |||||||||
| 인장 탄성 계수 | 16000ksi | 110317MPa | |||||||||
| 강성 계수 | 6000ksi | 41369MPa | |||||||||
제작 특성
CDA에서 제공하는 제작 특성 | |||||||||||
| 기술 | 적당 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 납땜 | 공정한 | ||||||||||
| 브레이징 | 좋은 | ||||||||||
| 옥시아세틸렌 용접 | 권장되지 않음 | ||||||||||
| 가스 차폐 아크 용접 | 공정한 | ||||||||||
| 코팅된 금속 아크 용접 | 권장되지 않음 | ||||||||||
| 스폿 용접 | 좋은 | ||||||||||
| 솔기 용접 | 좋은 | ||||||||||
| 맞대기 용접 | 좋은 | ||||||||||
| 냉간 가공 능력 | 가난한 | ||||||||||
| 열간 성형 능력 | 훌륭한 | ||||||||||
| 위조 가능성 등급 | 100 | ||||||||||
| 가공성 등급 | 30 | ||||||||||
열적 특성
CDA에서 제공하는 열적 특성 *온도는 화씨 단위로 측정됩니다. | |||||||||||
| 치료 | 최저한의* | 최고* | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 가열 냉각 | 800 | 1100 | |||||||||
| 뜨거운 치료 | 1100 | 1250년 | |||||||||
Common fabrication processesHot forging and pressing, machining
CDA에서 제공하는 일반적인 제조 프로세스