C87850 Description
Copper silicon UNS C87850 has a copper content of not less than 74%.
Tabulated below are the mechanical properties of UNS C87850 permanent mold cast alloy as a function of heat treatment.
| 気性 | 長い。 | ロックウェル | |||
|---|---|---|---|---|---|
| B | C | F | 30T | ||
| M05 | 21% | 74 | – | – | – |
| 16% | 70 | – | – | – | |
- C87850 Product description: Silicon brass
- Solids: Consult mill for sizes
- Tubes: Consult mill for sizes*
- Rectangles: Consult mill for sizes
- Standard lengths: 144″
- Shape/Form: Semi-finished, mill stock or near net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar
- Compliance: C87850 is compliant with key legislation including (1) Federal Safe Drinking Water Act – SDWA, (2) S. 3874 Federal Reduction of Lead in Drinking Water Act, (3) California AB1953, and (4) Vermont Act 193
*肉厚については工場にお問い合わせください
代表的な用途
Industrial: valve bodies for water
Marine: marine products
Plumbing: faucets, plumbing fittings, water meter cases
類似または同等の仕様
| CDA | ASTM | サエ | AMS | 連邦政府 | 軍隊 | 他の |
|---|---|---|---|---|---|---|
| C87850 | B505 B505M |
化学組成
| Cu% | Pb% | Sn% | 亜鉛% | Fe% | P% | 1で | Mn% | Sb% | そして％ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 75.00- 78.00 | 0.02*- 0.09 | 0.30 | レム。 | 0.10 | 0.05- 0.20 | 0.20 | 0.10 | 0.10 | 2.70～ 3.40 | ||
| Chemical composition according to ASTM B505/B505M-23*Pb content is greater than 0.02%. 1Ni value includes Co.Note: Cu + sum of named elements, 99.5% min. Single values represent maximums. | |||||||||||
被削性
| 銅合金 UNS No. | 被削性評価 | Density (lb/in3 at 68 ˚F) |
|---|---|---|
| C87850 | 70 | 0.3 |
機械的性質
| 引張強さ、最小 | Yield strength (at 0.5% extension under load,, min) | 伸び、2 インチまたは 50 mm 分 | ブリネル硬度（500kg荷重） | 備考 | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| クシ | MPa | クシ | MPa | % | minimum BHN | ||||||
| 65 | 448 | 25 | 172 | 8 | 103 | ||||||
| Mechanical properties according to ASTM B505/B505M-23 | |||||||||||
物理的特性
| 米国の慣例 | メトリック | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 融点 - 液体 | 1616 °F | 880 °C | |||||||||
| 融点 – 固相線 | 1571 °F | 855 °C | |||||||||
| 密度 | 068 °F で 0.3 ポンド/インチ3 | 8.3 gm/cm3 (20 °C) | |||||||||
| 電気伝導性 | 68 °F で 8% IACS | 0.046 MegaSiemens/cm at 20 °C | |||||||||
| 熱伝導率 | 21.8 Btu/sq ft/ft hr/°F at 68 °F | 37.8 W/m at 20 °C | |||||||||
| Coefficient of thermal expansion 68-212 | 10.3 · 10-6 per °F (68-212 °F) | 17.8 · 10-6 per °C (20-100 °C) | |||||||||
| 熱膨張係数 68-392 | 10.3 · 10-6/°F (68-392 °F) | 17.8 10-6/°C (20-200 °C) | |||||||||
| 熱膨張係数 68-572 | 10.4 · 10-6 per °F (68-572 °F) | 18 · 10-6 per °C (20-300 °C) | |||||||||
| 比熱容量 | 068 °F で .09 Btu/ポンド/°F | 377.1 J/kg (20 °C) | |||||||||
| 引張弾性率 | 15200 ksi | 104801 MPa | |||||||||
| CDA によって提供される物理的特性 | |||||||||||
製造特性
| 技術 | 適合性 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| はんだ付け | 素晴らしい | ||||||||||
| ろう付け | 素晴らしい | ||||||||||
| 酸素アセチレン溶接 | 良い | ||||||||||
| スポット溶接 | 良い | ||||||||||
| シーム溶接 | 良い | ||||||||||
| 突合せ溶接 | 良い | ||||||||||
| 冷間加工能力 | 貧しい | ||||||||||
| 熱間成形能力 | 素晴らしい | ||||||||||
| 被削性評価 | 70 | ||||||||||
| CDA によって提供される製造プロパティ | |||||||||||
熱特性
| Thermal properties provided by CDATemperature is measured in fahrenheit. **For stress relief, Solution treatment and annealing – time is measured in hours/inch of thickness. For precipitation heat treatment – time is measured in hours. |