UNS C69400 Silicon Red Brass
被削性The machinability rate of UNS C69400 silicon red brass alloys is 30.
溶接Soldering, brazing, oxyacetylene welding, spot welding, seam welding, and butt welding are considered as suitable welding processes for UNS C69400 alloy.
鍛造UNS C69400 alloy has a hot forgeability rating of 80 with the recommended hot working temperature ranging between 649 and 871°C (1200 and 1600°F).
熱間加工The hot working capacity of UNS C69400 silicon red brass alloy is excellent.
Cold Working
The cold working capacity of UNS C69400 is poor.
アニーリングThe annealing temperature of UNS C69400 silicon red brass alloy is between and 427 and 649°C (800 and 1200°F).
アプリケーションUNS C69400 silicon red brass alloy is used in heavy-duty mechanical components such as bearings, and used for pump components and valve stems.
C69400 Product description: Silicon red brass
C69400 brass is a brass formulated for primary forming into wrought products. Cited properties are appropriate for the H04 (full hard) temper.
It has a moderately low thermal conductivity among wrought brasses. In addition, it has a moderately low electrical conductivity and a moderately low melting temperature.
The graph bars on the material properties cards below compare C69400 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it’s 50% of the highest, and so on.
代表的な用途
Industrial: valve stems
類似または同等の仕様
| CDA | ASTM | サエ | AMS | 連邦政府 | 軍隊 | 他の |
|---|---|---|---|---|---|---|
| C69400 | B371 B371M |
化学組成
| Cu%1 | Pb% | 亜鉛% | Fe% | そして％ | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
Chemical composition according to ASTM B371/B371M-19 1Cu value includes Ag. 注: Cu + 指定元素の合計、99.5% 以上。単一の値は最大値を表します。 | |||||||||||
| 80.00- 83.00 | 0.30 | レム。 | 0.20 | 3.50～ 4.50 | |||||||
被削性
| 銅合金 UNS No. | 被削性評価 | 密度 (68 °F で lb/in3) |
|---|---|---|
| C69400 | 30 | 0.296 |
機械的性質
C69400
H04 HARD
サイズ範囲: 最大 1 インチまで
| 引張強さ、最小 | 降伏強度、荷重下で 0.5% 伸び、最小 | Elongation, in 4x diameter or thickness of specimen, min | ロックウェル「B」硬度 | 備考 | ||
|---|---|---|---|---|---|---|
| クシ | MPa | クシ | MPa | % | 典型的なBHN | |
| 80 | 550 | 40 | 250 | 15 | 95 | |
Size range: over 1″ to 2″ inclusive
| 引張強さ、最小 | 降伏強度、荷重下で 0.5% 伸び、最小 | Elongation, in 4x diameter or thickness of specimen, min | ロックウェル「B」硬度 | 備考 | ||
|---|---|---|---|---|---|---|
| クシ | MPa | クシ | MPa | % | 典型的なBHN | |
| 75 | 515 | 35 | 241 | 15 | 95 | |
Size range: over 2″
| 引張強さ、最小 | 降伏強度、荷重下で 0.5% 伸び、最小 | Elongation, in 4x diameter or thickness of specimen, min | ロックウェル「B」硬度 | 備考 | ||
|---|---|---|---|---|---|---|
| クシ | MPa | クシ | MPa | % | 典型的なBHN | |
| 65 | 450 | 35 | 241 | 15 | 95 | |
物理的特性
CDA によって提供される物理的特性 | |||||||||||
| 米国の慣例 | メトリック | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 融点 - 液体 | 1685 °F | 918 °C | |||||||||
| 融点 – 固相線 | 1510 °F | 821 °C | |||||||||
| 密度 | 0.296 lb/in3 at 68 °F | 8.19 gm/cm3 at 20 °C | |||||||||
| 比重 | 8.19 | 8.19 | |||||||||
| 電気伝導性 | 6.2% IACS at 68 °F | 0.04 MegaSiemens/cm at 20 °C | |||||||||
| 熱伝導率 | 15 Btu/sq ft/ft hr/°F at 68 °F | 25.98 W/m at 20 °C | |||||||||
| 熱膨張係数 68-572 | 11.2 · 10-6 per °F (68-572 °F) | 19.3 · 10-6 per °C (20-300 °C) | |||||||||
| 比熱容量 | 068 °F で .09 Btu/ポンド/°F | 377.1 J/kg (20 °C) | |||||||||
| 引張弾性率 | 16000 ksi | 110310MPa | |||||||||
製造特性
CDA によって提供される製造プロパティ | |||||||||||
| 技術 | 適合性 | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| はんだ付け | 素晴らしい | ||||||||||
| ろう付け | 素晴らしい | ||||||||||
| 酸素アセチレン溶接 | 良い | ||||||||||
| スポット溶接 | 良い | ||||||||||
| シーム溶接 | 良い | ||||||||||
| 突合せ溶接 | 良い | ||||||||||
| 冷間加工能力 | 貧しい | ||||||||||
| 熱間成形能力 | 素晴らしい | ||||||||||
| 鍛造性評価 | 80 | ||||||||||
| 被削性評価 | 30 | ||||||||||
熱特性
CDA によって提供される熱特性 ※温度は華氏で測定されます。 | |||||||||||
| 処理 | 最小* | 最大* | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| アニーリング | 800 | 1200 | |||||||||
| ホットトリートメント | 1200 | 1600 | |||||||||
Common fabrication processesForging, screw machining
CDAが提供する一般的な製造プロセス