This document provides a comprehensive comparison between the UNSC95500and UNSC95400copper alloys, detailing their chemical composition, mechanical properties, temperature performance, industry applications, shapes and sizes, production standards, processing techniques, advantages and disadvantages, and similar products, all presented in table formats.
化学組成
要素
UNS C95500 Content (%)
UNS C95400 Content (%)
銅、Cu
78.0
83.0
アルミニウム、アル
10.0 – 11.5
10.0
ニッケル、Ni
3.0 – 5.50
1.0 – 1.5
鉄、鉄
3.0 – 5.0
3.0 – 5.0
マンガン、ミネソタ州
3.50
0.5
機械的性質
UNS C95500
財産
メトリック
インペリアル
Hardness, Brinell (sand cast)
192
192
抗張力
585 – 660 MPa
84800 – 95700 psi
降伏強さ
240 – 360 MPa
34800 – 52200 psi
Elongation at Break
5.00% – 25.00%
5.00% – 25.00%
Compressive Strength
240 – 690 MPa
34800 – 100000 psi
UNS C95400
財産
メトリック
インペリアル
硬度、ブリネル
170 – 210
170 – 210
抗張力
380 – 550 MPa
55000 – 80000 psi
降伏強さ
200 – 300 MPa
29000 – 43500 psi
Elongation at Break
10.00% – 30.00%
10.00% – 30.00%
Compressive Strength
200 – 500 MPa
29000 – 72500 psi
さまざまな温度でのパフォーマンス
財産
C95500
C95400
Thermal Expansion Coefficient
16.2 µm/m°C
16.5 µm/m°C
熱伝導率
42.0 W/mK
35.0 W/mK
産業用途
応用
C95500
C95400
Marine Components
Shafting, fittings
Propellers, valves
電気
Electrical connectors
Electrical components
自動車
Transmission parts
Gears and bushings
形状とサイズ
形
C95500
C95400
Standard Forms
Rods, tubes, castings
Rods, plates, tubes
Custom Sizes
Available on request
Available on request
製造基準
標準
C95500
C95400
ASTM
B148, B271
B148, B271
MIL
Not applicable
MIL B-24480
Processing Techniques
溶接
技術
C95500
C95400
Preferred Methods
Brazing, soldering
Brazing, soldering
推奨されません
酸素アセチレン溶接
酸素アセチレン溶接
被削性
Alloy Rating (C36000 = 100)
C95500
C95400
被削性評価
50%
60%
熱処理
熱処理
C95500
C95400
Stress Relieving Temperature
316°C (600°F)
316°C (600°F)
Reaction to Heat Treatment
Does not react significantly
Slight improvement in strength
長所と短所
C95500
利点
短所
High strength and hardness
Higher cost per unit
Good fatigue resistance
More complex processing
C95400
利点
短所
優れた耐食性
Lower strength than C95500
良好な機械加工性
Limited applications in high-stress environments
Similar Products
Similar Products
C95500
C95400
Other Copper Alloys
C95600, C95200
C95200, C93200
Bronze Alloys
Aluminum bronze, tin bronze
Aluminum bronze, tin bronze
This comparison provides a detailed overview of the properties and characteristics of UNS C95500 and UNS C95400 copper alloys, assisting in material selection for specific applications. If you have further inquiries or require additional information, please feel free to ask!