This article compares the characteristics of UNS C63200 and UNS C95800 copper alloys, detailing their chemical compositions, mechanical properties, performance at different temperatures, industry applications, shape, size, production standards, and additional relevant factors.
化学組成
要素
C63200 (%)
C95800 (%)
アルミニウム(Al)
8.7 – 9.5
8.5 – 9.5
ニッケル(Ni)
4.0 – 4.8
4.0 – 5.0
鉄(Fe)
3.5 – 4.3
3.5 – 4.5
マンガン(Mn)
1.2～2.0
0.8 – 1.5
シリコン（Si）
0.1
0.1
鉛(Pb)
0.02
0.03
銅
バランス
79
機械的性質
財産
C63200
C95800
硬度（ロックウェルB）
85-95
85-90
抗張力
550MPa
620 MPa
降伏強さ
300 MPa
380 MPa
Elongation at Break
10%
8%
弾性率
117 GPa
117 GPa
シャルピーインパクト
25.0 J
15.0 J
被削性
70
40
さまざまな温度でのパフォーマンス
財産
C63200
C95800
融点
1033°C (1911°F)
1060°C (1940°F)
熱伝導率
50.0 W/mK (346 BTU in/hr.ft²°F)
40.0 W/mK (276 BTU in/hr.ft²°F)
Thermal Expansion Coefficient
16.3 µm/m°C
16.5 µm/m°C
産業用途
応用
C63200
C95800
Marine Components
Yes
Yes
Pump and Valve Components
Yes
Yes
Electrical Connectors
Limited
Limited
Heavy Machinery Parts
Limited
Yes
形状とサイズ
Attribute
C63200
C95800
Available Shapes
Rods, Bars
Rods, Bars
Standard Sizes
Various
Various
Common Forms
Sheet, Plate
Sheet, Plate
製造基準
標準
C63200
C95800
ASTM
B505, B150
B505, B150
私のように
SFA 5.7
SFA 5.7
サエ
J461, J463
J461, J463
溶接・加工
加工方法
C63200
C95800
Welding Compatibility
Good (with precautions)
Limited
Preferred Welding Method
Gas shielded, resistance
Somewhat difficult
研磨
Good polishing capability
Moderate polishing capability
熱処理
Yes
Yes
冷間加工
Moderate capacity
Limited
長所と短所
Attribute
C63200
C95800
利点
Good strength, corrosion resistant
Excellent wear resistance, high strength
短所
Lower wear resistance compared to C95800
Higher cost, lower machinability
Similar Products
Similar Products
プロパティ
Copper Nickel Alloys
Good corrosion resistance, suitable for marine applications.
Aluminium Bronze Alloys
High strength and corrosion resistance, often used in similar applications.
Comparison of Similar Products
製品
耐食性
強さ
アプリケーション
UNS C63200
高い
適度
Marine, Pumps, Valves
UNS C95800
より高い
高い
Pumps, Heavy Machinery
Copper Nickel Alloys
非常に高い
適度
Marine, Plumbing
結論
In conclusion, both UNS C63200 and UNS C95800 copper alloys exhibit unique properties that make them suitable for different applications. C63200 is characterized by its good strength and corrosion resistance, making it a reliable option for marine components. In contrast, C95800 provides superior wear resistance and is better suited for high-stress applications, particularly in heavy machinery. Understanding these distinctions will facilitate informed choices in material selection for various engineering requirements. If you have any further questions or need additional information, feel free to ask!