UNS C65100 (CW115C) Silicon Bronze
C65100 bronze is a bronze formulated for primary forming into wrought products. CW115C is the EN numeric designation for this material. C65100 is the UNS number. Additionally, the EN chemical designation is CuSi1. And the common industry name is Low-Silicon Bronze B.
It has the lowest embodied energy and can have a moderately low tensile strength among wrought bronzes.
The properties of C65100 bronze include nine common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare C65100 bronze to: wrought bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it’s 50% of the highest, and so on.
Solids: 3/8″ to 2″ O.D.
Hex: 3/8″ to 2″ O.D.
Lunghezze standard: 144″
Usi tipici
Electrical: conduit, motor (rotor bars), pole line hardware
Fasteners: bolts, cable clamps, cap screws, fasteners, machine screws, nuts, rivets, screws, u bolts
Industrial: heat exchanger tube, hydraulic pressure lines, oil refinery plumbing tube, welding rod
Marino: hardware
Specifica simile o equivalente
| CDA | ASMA | SAE | AMS | Federale | Militare | Altro |
|---|---|---|---|---|---|---|
| C65100 | B98 B98M |
Composizione chimica
| Cu%1 | Pb% | Zn% | Fe% | Mn% | E% | ||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
1Cu value includes Ag. Nota: Cu + somma degli elementi nominati, 99,5% min. I singoli valori rappresentano i massimi. | |||||||||||
| REM. | 0.05 | 1,50 | 0.80 | 0.70 | 0.80- 2.00 | ||||||
lavorabilità
| Lega di rame N. UNS | Grado di lavorabilità | Densità (lb/in3 a 68 °F) |
|---|---|---|
| C65100 | 30 | 0.316 |
Proprietà meccaniche
C65100
H02 semiduro
Size range: up to 1/2″ rod inclusive
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 55 | 380 | 20 | 140 | 11 | 60-85 | |
Size range: over 1/2″ to 2″ rod inclusive
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 55 | 380 | 20 | 140 | 12 | 60-85 | |
C65100
H04 difficile
Size range: up to 1/2″ rod inclusive
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 65 | 450 | 35 | 241 | 8 | 65-90 | |
Size range: over 1/2″ to 2″ rod inclusive
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 65 | 450 | 35 | 241 | 10 | 65-90 | |
C65100
H06 extra hard
Size range: up to 1/2″ rod inclusive
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 85 | 585 | 55 | 380 | 6 | 75-95 | |
Gamma di dimensioni: asta da oltre 1/2″ a 1″ inclusa
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 75 | 515 | 45 | 310 | 8 | 75-95 | |
Size range: over 1″ to 1 1/2″ rod inclusive
| Resistenza alla trazione, min | Carico di snervamento, allo 0,5% di estensione sotto carico, min | Allungamento, in 2 pollici o 50 mm min | Durezza Rockwell “B”. | la lega ha il doppio della sua resistenza alla compressione | ||
|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | min al massimo HRB | |
| 75 | 515 | 40 | 275 | 8 | 75-95 | |
Proprietà fisiche
Proprietà fisiche fornite da CDA | |||||||||||
| Consuetudine statunitense | Metrica | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Punto di fusione – liquido | 1940 °F | 1060 °C | |||||||||
| Punto di fusione – solidus | 1890 °F | 1032 °C | |||||||||
| Densità | 0.316 lb/in3 at 68 °F | 8.75 gm/cm3 at 20 °C | |||||||||
| Peso specifico | 8.75 | 8.75 | |||||||||
| Conduttività elettrica | 12% IACS a 20 °C | 00,07 MegaSiemens/cm a 20 °C | |||||||||
| Conduttività termica | 33 Btu/sq ft/ft hr/°F at 68 °F | 57.1 W/m at 20 °C | |||||||||
| Coefficiente di dilatazione termica 68-572 | 9.9 · 10-6 per °F (68-572 °F) | 17.1 · 10-6 per °C (20-300 °C) | |||||||||
| Capacità termica specifica | 00,09 Btu/lb/°F a 68 °F | 377,1 J/kg a 20 °C | |||||||||
| Modulo di elasticità a trazione | 17000 ksi | 117212MPa | |||||||||
| Modulo di rigidità | 6400 ksi | 44127MPa | |||||||||
Proprietà di fabbricazione
Proprietà di fabbricazione fornite da CDA | |||||||||||
| Tecnica | adeguatezza | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| saldatura | Eccellente | ||||||||||
| brasatura | Eccellente | ||||||||||
| Saldatura ossiacetilenica | Bene | ||||||||||
| Saldatura ad arco protetto con gas | Eccellente | ||||||||||
| Saldatura ad arco di metalli rivestiti | Equo | ||||||||||
| Saldatura a punti | Eccellente | ||||||||||
| Saldatura continua | Bene | ||||||||||
| Saldatura di testa | Eccellente | ||||||||||
| Capacità di essere lavorato a freddo | Eccellente | ||||||||||
| Capacità di essere formato a caldo | Eccellente | ||||||||||
| Grado di lavorabilità | 30 | ||||||||||
Proprietà termali
Proprietà termiche fornite da CDA *La temperatura è misurata in Fahrenheit. |