C63000 Nickel Aluminum Bronze Product Introduction
- Composizione: Cu: 81.0%, Al: 10.0%, Ni: 5.0%, Fe: 3.0%, Mn: 1.0%
- Proprietà meccaniche: Tensile Strength: 900 MPa, Yield Strength: 550 MPa, Elongation: 15%, Hardness (Rockwell B): 80
- Performance: Excellent corrosion resistance in seawater and acidic environments, with consistent mechanical properties across temperatures.
- Applicazioni: Widely used in marine (propellers, shafts), aerospace (bushings, valves), and industrial sectors (bearings, gears).
- Shapes & Sizes: Available in rods (6 mm to 200 mm diameter), bars, plates (5 mm to 50 mm thickness), and tubes (10 mm to 150 mm OD).
- Standard di produzione: Conforms to ASTM B150/B150M and SAE J461 standards.
C63000 Nickel Aluminum Bronze Product Introduction
Composizione chimica
| Elemento | Composizione (%) |
|---|---|
| Rame | 81.0 |
| Alluminio (Al) | 10.0 |
| Nichel (Ni) | 5.0 |
| Ferro (Fe) | 3.0 |
| Manganese (Mn) | 1.0 |
Proprietà meccaniche
| Proprietà | Valore |
|---|---|
| Resistenza alla trazione | 900 MPa (130 ksi) |
| Limite di snervamento (compensazione dello 0,2%) | 550 MPa (80 ksi) |
| Allungamento | 15% |
| Durezza (Rockwell B) | 80 |
Prestazioni a diverse temperature
C63000 Nickel Aluminum Bronze exhibits good mechanical properties across a range of temperatures, suitable for applications in both high and low temperature environments.
Applicazioni industriali
C63000 Nickel Aluminum Bronze is widely used in:
- Marine applications: propellers, shafts, fittings.
- Aerospace: landing gear bushings, valve components.
- Industrial machinery: bearings, gears, bushings.
- Chemical processing equipment.
Forma e dimensione
C63000 Nickel Aluminum Bronze is available in various shapes and sizes, including:
- Rods: Diameter ranging from 6 mm to 200 mm.
- Barre: Barre quadre e tonde di varie dimensioni.
- Lastre: Spessori che vanno da 5 mm a 50 mm.
- Tubes: OD ranging from 10 mm to 150 mm.
Standard di produzione
C63000 Nickel Aluminum Bronze conforms to international standards such as:
- ASTM B150/B150M: Specifiche standard per aste, barre e forme in bronzo-alluminio.
- SAE J461: Leghe di rame lavorate e fuse.
Standard e gradi corrispondenti
| Paese/regione | Standard | Gradi corrispondenti |
|---|---|---|
| Stati Uniti d'America | ASTM B150/B150M | C63000 |
| Europa | BS EN 12163, BS EN 12420 | CuAl10Ni5Fe4 |
| Giappone | HE H3250 | C6300 |
Saldatura, Lavorazione, Lucidatura
C63000 Nickel Aluminum Bronze can be welded using various methods such as gas tungsten arc welding (GTAW) and gas metal arc welding (GMAW). It is also suitable for machining, polishing, and can be heat treated to improve its mechanical properties.
Trattamenti termici e lavorazioni a freddo
C63000 Nickel Aluminum Bronze can be heat treated to improve its strength and hardness. Cold processing methods such as cold rolling and cold drawing can enhance its mechanical properties.
Vantaggi e svantaggi
| Vantaggi | Svantaggi |
|---|---|
| Elevata resistenza e tenacità | Higher cost compared to other bronze alloys |
| Excellent corrosion resistance | Limited availability in some regions |
| Buona resistenza all'usura | Requires expertise for welding and processing |
| Suitable for various temperatures and environments |
Prodotti simili e confronto
| Tipo/proprietà della lega | C63000 Bronzo al nichel-alluminio | C95400 Bronzo alluminio | C62300 Bronzo alluminio |
|---|---|---|---|
| Composizione (%) | Cu: 81.0, Al: 10.0, Ni: 5.0 | Cu: 85.0, Al: 11.0 | Cu: 88,0, Al: 10,0 |
| Resistenza alla trazione (MPa) | 900 | 500 | 600 |
| Carico di snervamento (MPa) | 550 | 200 | 250 |
| Applicazioni | Marino, aerospaziale, industriale | Cuscinetti, ingranaggi, boccole | Valvole, raccordi |
Conclusione
C63000 Nickel Aluminum Bronze is a versatile alloy known for its exceptional mechanical properties, corrosion resistance, and suitability for various industrial applications. Its composition and performance make it a preferred choice in marine environments, aerospace, and industrial machinery where strength, durability, and resistance to wear are critical factors.