Overview of copper alloy wire
About Lion Copper Alloy Wire
Properties and uses of copper alloy wire
Zutaten
Copper alloy wire is a copper alloy product, usually composed of copper and other alloy elements. Common copper alloys include brass, tin bronze, aluminum bronze, etc. These copper alloys are high-strength alloy materials with good electrical conductivity and corrosion resistance.
Leistung
Copper alloy wire has good strength, conductivity and corrosion resistance, and can meet the different levels of conductivity requirements of different electrical appliance industries. By adding alloying elements, the hardness and strength of copper alloys can be improved, and their wear resistance and corrosion resistance can be improved.
Application fields
Copper alloy wire is widely used in the manufacturing of conductive parts, springs, valves, gears and other components in the electrical industry, refrigeration equipment, ships, automobiles and other fields. In addition, copper alloy wire is also suitable for use in high temperature and high pressure applications, such as slag valve components in the petrochemical industry.
Vorteile und Nachteile
Compared with pure copper wire, copper alloy wire has higher strength and hardness, and better wear resistance and corrosion resistance. However, compared with pure copper wire, the electrical conductivity of copper alloy wire will be slightly reduced, and the price is also higher. Therefore, the choice of copper alloy versus pure copper requires trade-offs based on specific requirements.
To sum up, copper alloy wire is an alloy wire widely used in the electrical industry and other fields. It has good electrical conductivity and corrosion resistance. Adding alloying elements can improve its properties and hardness, but can also affect its conductivity and price. In practical applications, appropriate materials need to be selected based on specific requirements.
1、Brass wire rod for the cutting of high precision new materials
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | ||||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Allowable deviation(mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | |||||||||||||||||
H60 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 1.2 | ±0,02 | ≥330 | 18 | 58.0~60.0 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H62 | C2800 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 1.2 | ±0,02 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | 18 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H63 | C2720 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 1.2 | ±0,02 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | 18 | 62.0~65.0 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H65 | C2680 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 1.2 | ±0,02 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | 18 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.5 |
Application field: brass wire rod for copper alloy high precision new materials processing, mainly used for slow-wire-cut mould cutting.
2、 Electric connector
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
H62 | C2800 | Y4 | 1/4H | 0.5~2.4x 4.5~11.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥15 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H63 | C2720 | Y4 | 1/4H | 0.5~2.5x 4.5~11.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥15 | 62.0~65.0 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H65 | C2680 | Y2 | 1/2 Std | 0.7~2.0x 5.0~10.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥16 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
H68 | C2620 | Y2 | 1/2 Std | 1.0~2.0x 6.0~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥16 | 67.0~70.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
H80 | C2400 | Y2 | 1/2 Std | 1.5~2.0x 4.5~7.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥16 | 79.0~81.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
Note: We can provide customized products according to customers’ needs. Allowable deviation in product size: thickness ±0.02mm, width ±0.03mm.
Application Field: plug and connector for electric appliances
3、High precision copper alloy Y-shaped zipper wire
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Vickers Hardness(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
H65 | C2680 | UND | JOMINY HÄRTBARKEIT | 3#、4#、5# | ≥160 | ≥1 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
H85 | C2300 | UND | JOMINY HÄRTBARKEIT | 3#、4#、5# | ≥130 | ≥1 | 84.0~86.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
Note: Meet environment standards and EU ROSH standard. Allowable deviation in product size: ±0.03mm. Packaging: Spool
Application Field: Zipper products for clothing and bags.
4、Flat zipper wire
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
H63 | C2720 | Y2 | 1/2 Std | 3#、4#、5#、7#、8#、10# | ≥350 | ≥6 | 62.0~65.0 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H65 | C2680 | Y2 | 1/2 Std | 3#、4#、5#、7#、8#、10# | ≥380 | ≥7 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
Note: We can provide customized products according to customers’ needs.
Meet environment standards and EU ROSH standard. Allowable deviation in product size: thickness ±0.02mm, width ±0.03mm. Packaging weight: 40Kg.
Application Field: Zipper products for clothing and bags.
5、Copper alloy flat wire
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
H65 | C2680 | Y2 | 1/2 Std | 0.7~1.3x 5.9~12.0 | ≥300 | 10 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
H85 | C2300 | Y2 | 1/2 Std | 0.8~1.2x 6.0~12.0 | ≥280 | ≥12 | 84.0~86.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
Note: We can provide customized products according to customers’ needs.
Meet environment standards and EU ROSH standard. Allowable deviation in product size: thickness ±0.02mm, width ±0.03mm. Packaging weight: 40Kg.
Application Field: Zipper heads for zippers used in clothing and bags.
6、Copper alloy wire for spring products
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Specification(mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
H62 | C2800 | T | Sch | 0.45~1.4 | ≥800 | ≥4 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H63 | C2720 | T | Sch | 0.5~2.0 | ≥750 | ≥4 | 62.0~65.0 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H65 | C2680 | T | Sch | 0.6~1.4 | ≥800 | ≥4 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
QSn6.5-0.1 | T51510 | T | Sch | 0.4~1.5 | ≥800 | ≥4 | Residual | 0.02 | 0.02 | — | — | 6.0~7.0 | — | 0.1~0.25 | 0.3 | 0.4 |
Note: We can provide customized products according to customers’ needs. | ||||||||||||||||
Application Field: Spring product for clothing buttons and hardware accessories. |
7、Copper alloy inflating valve for tires
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | ||||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Allowable deviation(mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | |||||||||||||||||
H62 | C2800 | Y4 | 1/4H | 5.2~7.9 | ±0,02 | ≥330 | ≥14 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
We can provide customized products according to customers’ needs.
Application Field: inflating valves in tires for bicycles, motorcycles and automobiles.
8、Copper alloy bar for screws
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | ||||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Allowable deviation(mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | |||||||||||||||||
H62 | C2800 | Y4 | 1/4H | 1.3~11.0 | ±0,02 | ≥330 | ≥8 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
H65 | C2680 | Y4 | 1/4H | 1.3~9.0 | ±0,02 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥8 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
H68 | C2620 | Y4 | 1/4H | 1.2~9.0 | ±0,02 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥8 | 67.0~70.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
H70 | C2600 | Y4 | 1/4H | 3.0~8.0 | ±0,02 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | ≥8 | 68.5~71.5 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
Note: We can provide customized products according to customers’ needs.
Application Field: various screws used for hardware products.
9、Copper alloy wire rod for ornaments
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Specification(mm) | Tensile Strength(N/mm²) | Verlängerung(%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
H90 | C2200 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.3~5.0 | ≥260 | 18 | 88.0~91.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.2 |
UND | JOMINY HÄRTBARKEIT | 0.8~4.5 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | — | ||||||||||||
H62 | C2800 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.3~9.0 | ≥255 | 18 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
UND | JOMINY HÄRTBARKEIT | 0.4~6.5 | ≥330 | — | ||||||||||||
H65 | C2680 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.35~9.0 | ≥250 | ≥28 | 63.5~68.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
UND | JOMINY HÄRTBARKEIT | 0.7~9.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | — | ||||||||||||
H68 | C2620 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.3~5.0 | ≥250 | ≥28 | 67.0~70.0 | 0.1 | 0.03 | — | — | — | 0.5 | — | Residual | 0.3 |
BZn8-25 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ≥320 | Ø = Dicke bzw. Drahtdurchmesser in mm | 60.0~63.0 | 0.3 | 0.03 | — | — | — | 7.2~9.2 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥420 | ≥6 | ||||||||||||
BZn10-25 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ≥320 | Ø = Dicke bzw. Drahtdurchmesser in mm | 60.0~63.0 | 0.3 | 0.03 | — | — | — | 9.2~11.2 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥420 | ≥6 | ||||||||||||
BZn12-23 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ≥320 | Ø = Dicke bzw. Drahtdurchmesser in mm | 63.0~66.0 | 0.3 | 0.03 | — | — | — | 11,0 ~ 13,0 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥420 | ≥6 | ||||||||||||
BZn15-20 | T74600 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | Ø = Dicke bzw. Drahtdurchmesser in mm | 63.5~68.0 | 0.5 | 0.02 | — | — | — | 13.5~16.5 | — | Residual | 0.9 |
Y2 | 1/2 Std | 0.3~7.0 | 490 | — | ||||||||||||
BZn18-20 | T76300 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | Ø = Dicke bzw. Drahtdurchmesser in mm | 60.0~63.0 | 0.3 | 0.03 | — | — | — | 16.5~19.5 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥440 | — | ||||||||||||
BZn18-18 | C75200 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | Ø = Dicke bzw. Drahtdurchmesser in mm | 63.0~66.5 | 0.25 | 0.05 | — | — | — | 16.5~19.5 | — | Residual | 1.3 |
Y2 | 1/2 Std | 0.3~7.0 | ≥440 | — | ||||||||||||
QSn6.5-0.1 | T51510 | Y2 | 1/2 Std | 1.0~8.0 | ≥460 | ≥4 | Residual | 0.02 | 0.02 | — | — | 6.0~7.0 | — | 0.1~0.25 | 0.3 | 0.4 |
QSn5-0.2 | T51000 | Y2 | 1/2 Std | 1.0~7.0 | ≥460 | ≥4 | Residual | 0.1 | 0.05 | — | — | 4.2~5.8 | — | 0.03~0.35 | 0.3 | 0.95 |
Note: We can provide customized products according to customers’ needs. Allowable deviation in product size: ±0.02mm. Application Field: mainly used for the production of hardware ornaments like necklace, bracelet and earrings. |
10、Copper alloy wire rod for hardware, glasses, Musical Instruments,etc
Grad | Bundesland | Mechanische Eigenschaften | Chemical Composition(%) | |||||||||||||
wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | wo das Material anfängt, dünner zu werden und wie Toffee zu ziehen | JIS | Spezifikation (mm) | Tensile Strength(N/mm²) | Verlängerung (%) | Mit | Fe | Pb | Al | Mn | Sn | Ni | P | Zn | Impurity Volume |
Not more than | ||||||||||||||||
BZn8-25 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ≥320 | Ø = Dicke bzw. Drahtdurchmesser in mm | 60.0~63.0 | 0.3 | 0.03 | — | — | — | 7.2~9.2 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥420 | ≥6 | ||||||||||||
BZn10-25 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ≥320 | Ø = Dicke bzw. Drahtdurchmesser in mm | 60.0~63.0 | 0.3 | 0.03 | — | — | — | 9.2~11.2 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥420 | ≥6 | ||||||||||||
BZn12-23 | — | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ≥320 | Ø = Dicke bzw. Drahtdurchmesser in mm | 63.0~66.0 | 0.3 | 0.03 | — | — | — | 11,0 ~ 13,0 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥420 | ≥6 | ||||||||||||
BZn15-20 | T74600 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | Ø = Dicke bzw. Drahtdurchmesser in mm | 63.5~68.0 | 0.5 | 0.02 | — | — | — | 13.5~16.5 | — | Residual | 0.9 |
Y2 | 1/2 Std | 0.3~7.0 | 490 | — | ||||||||||||
BZn18-20 | T76300 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | Ø = Dicke bzw. Drahtdurchmesser in mm | 60.0~63.0 | 0.3 | 0.03 | — | — | — | 16.5~19.5 | — | Residual | 0.8d |
Y2 | 1/2 Std | 0.3~7.0 | ≥440 | — | ||||||||||||
BZn18-18 | C75200 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.5~8.0 | ist ein niedrig legierter, hochfester Baustahl nach chinesischem GB-Standard | Ø = Dicke bzw. Drahtdurchmesser in mm | 63.0~66.5 | 0.25 | 0.05 | — | — | — | 16.5~19.5 | — | Residual | 1.3 |
Y2 | 1/2 Std | 0.3~7.0 | ≥440 | — | ||||||||||||
H62 | C2800 | WNM400 Beschreibung | verglichen mit dem normalen Prozess von | 0.3~9.0 | ≥255 | 18 | 60.5~63.5 | 0.fünfzehn | 0.08 | — | — | — | 0.5 | — | Residual | 0.5 |
Y2 | 1/2 Std | 0.4~6.5 | 410 | ≥4 | ||||||||||||
QSn6.5-0.1 | T51510 | Y2 | 1/2 Std | 1.0~8.0 | ≥460 | ≥4 | Residual | 0.02 | 0.02 | — | — | 6.0~7.0 | — | 0.1~0.25 | 0.3 | 0.4 |
QSn5-0.2 | T51000 | Y2 | 1/2 Std | 1.0~7.0 | ≥460 | ≥4 | Residual | 0.1 | 0.05 | — | — | 4.2~5.8 | — | 0.03~0.35 | 0.3 | 0.95 |
Note: We can provide customized products according to customers’ needs. Allowable deviation in product size: ±0.02mm. | ||||||||||||||||
Application Field: mainly used for making glasses accessories, electrical plug-ins, musical instruments accessories,etc. |