Incoloy 901 Description
Incoloy 901 A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening.
The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C).
A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Incoloy 901 (UNS N09901/Din 1.4898),
Alloy 901(Incoloy) has good corrosion resistance to the atmospheres normally found in jet engine operations.
Incoloy 901 Chemical composition:
سبيكة | ٪ | ني | مع | ال | Fe | أنت | شارك | Mn | س | ج | و | ص | سجل تجاري | مو | ب |
901- أقراص | دقيقة. | 40.0 | 2.35 | 11.0 | 5.0 | 0.01 | |||||||||
الأعلى. | 45.0 | 0.50 | 0.35 | الرصيد | 3.10 | 1.0 | 1.0 | 0.03 | 0.10 | 0.60 | 0.03 | 14.0 | 7.0 | 0.02 |
Incoloy 901 Physical properties:
سمك 12-300 مم × عرض 200-2300 مم | 8.14 g/cm3 |
نقطة الانصهار | 1280-1345℃ |
Incoloy 901 minimum mechanical properties in the room temperature:
حالة | قوة الشد Rm N / مم 2 | ستكون الخواص الميكانيكية مختلفة RP0.2N/mm2 | استطالة A5 % |
901- أقراص | 1034 | 689 | 12 |
وصف
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
المقاومة للتآكل
Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
قابلية العمل
العمل الساخن
Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
قابلية اللحام
Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.
(Incoloy 901) Regular shape for all kinds of alloys | |||
| استمارة | تخصيص | نموذج التوريد | آحرون |
| ورقة | Thickness：0.40-4.75mm，General Width：1000、1219、1500mm | ملف كامل أو قطعة منه | Cold Annealed，Surface 2B、2E |
| لوحة | Thickness：4.76-60mm，Width：1500、2000、2500mm，Length：3000、6000、8000、8500mm（Under 10mm plate can be coiled） | ملف كامل أو قطعة منه | Single hot rolling，Solid solution annealed state，Surface 1D |
| حزام | Thickness：0.10-3.0mm，Width：50-500mm | ملف كامل أو حجم محدد | Cold Annealed，Surface 2B、2E |
| Bar & Rod | Rolled barΦ5-45mm，Length≤1500mm | Polished Bar（circle、Square） | Solution annealing,descaling |
| Forged barΦ26-245mm，Length≤4000mm | |||
| أنبوب اللحام | Outer diameterΦ4.76-135mm，Wall Thickness0.25-4.00mm，Length：≤35000 mm | قاعدة على الاحتياجات الخاصة بك | |
| أنبوب السلس | Outer diameterΦ3-114mm，Wall Thickness0.2-4.5mm | قاعدة على الاحتياجات الخاصة بك | |
| الأسلاك | القطر الخارجي 0.1-13mm | قاعدة على الاحتياجات الخاصة بك | Ni & Ni alloy, Ti & Ti alloy |
| قطعة مزورة | discs,rings,squares,blocks,slabs | قاعدة على الاحتياجات الخاصة بك | Steel, Alloy |
| الشفاه | جميع أنواع الفلنجات | قاعدة على الاحتياجات الخاصة بك | Steel, Alloy |
| مواد لحام | سلك لفائف Φ0.025mm-1.6mm | قاعدة على الاحتياجات الخاصة بك | Certificate of Origin：America, Sweden, Britain, Germany, Austria, Italy, France. |
| سلك مستقيم 1.6mm-4.0mm | |||
| قضيب اللحامΦ1.2mm-4.0mm | |||
| الة النفخ | Elbow, three links, four links, different diameter size | قاعدة على الاحتياجات الخاصة بك | Ni & Ni alloy, Ti & Ti alloy |
| صفح مستعبدين متفجر | سمك الورقة الخام 2mm | قاعدة على الاحتياجات الخاصة بك | Ni & Ni alloy, Ti & Ti alloy |
منتجات مماثلة: INCOLOY 800H / HT 825 مشروع محل تجريبى 825