C87850 Description
Copper silicon UNS C87850 has a copper content of not less than 74%.
Tabulated below are the mechanical properties of UNS C87850 permanent mold cast alloy as a function of heat treatment.
| لين، لطف، هدأ | Elong. | روكويل | |||
|---|---|---|---|---|---|
| ب | ج | F | 30T | ||
| M05 | 21% | 74 | - | - | - |
| 16% | 70 | - | - | - | |
- C87850 Product description: Silicon brass
- Solids: Consult mill for sizes
- Tubes: Consult mill for sizes*
- Rectangles: Consult mill for sizes
- Standard lengths: 144″
- Shape/Form: Semi-finished, mill stock or near net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar
- Compliance: C87850 is compliant with key legislation including (1) Federal Safe Drinking Water Act – SDWA, (2) S. 3874 Federal Reduction of Lead in Drinking Water Act, (3) California AB1953, and (4) Vermont Act 193
* استشارة مطحنة لسمك الجدار
الاستخدامات النموذجية
Industrial: valve bodies for water
Marine: marine products
Plumbing: faucets, plumbing fittings, water meter cases
مواصفات مماثلة أو معادلة
| CDA | من | SAE | AMS | الفيدرالية | جيش | آخر |
|---|---|---|---|---|---|---|
| C87850 | B505 B505M |
أدوات معالجة البلاستيك وقوالب الصب بالضغط
| النحاس% | الرصاص% | نسبة القصدير | الزنك٪ | الحديد% | ف٪ | في 1 | Mn% | بينالي الشارقة٪ | و٪ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 75.00- 78.00 | 0.02*- 0.09 | 0.30 | ريم. | 0.10 | 0.05- 0.20 | 0.20 | 0.10 | 0.10 | 2.70- 3.40 | ||
| Chemical composition according to ASTM B505/B505M-23*Pb content is greater than 0.02%. 1Ni value includes Co.Note: Cu + sum of named elements, 99.5% min. Single values represent maximums. | |||||||||||
آلية
| سبائك النحاس رقم UNS. | تصنيف قابلية التشغيل الآلي | Density (lb/in3 at 68 ˚F) |
|---|---|---|
| C87850 | 70 | 0.3 |
الخواص الميكانيكية
| قوة الشد، دقيقة | Yield strength (at 0.5% extension under load,, min) | الاستطالة، في 2 بوصة أو 50 ملم دقيقة | صلابة برينل (حمولة 500 كجم) | ملاحظات | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | minimum BHN | ||||||
| 65 | 448 | 25 | 172 | 8 | 103 | ||||||
| Mechanical properties according to ASTM B505/B505M-23 | |||||||||||
الخصائص الفيزيائية
| العادة الأمريكية | قياس | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| نقطة الانصهار - السائل | 1616 °F | 880 °C | |||||||||
| نقطة الانصهار - الصلبة | 1571 °F | 855 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 0.3 lb/in3 at 68 °F | 8.3 gm/cm3 at 20 °C | |||||||||
| التوصيل الكهربائي | 8% IACS at 68 °F | 0.046 MegaSiemens/cm at 20 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 21.8 Btu/sq ft/ft hr/°F at 68 °F | 37.8 W/m at 20 °C | |||||||||
| Coefficient of thermal expansion 68-212 | 10.3 · 10-6 per °F (68-212 °F) | 17.8 · 10-6 per °C (20-100 °C) | |||||||||
| معامل التمدد الحراري 68-392 | 10.3 · 10-6 per °F (68-392 °F) | 17.8 · 10-6 per °C (20-200 °C) | |||||||||
| معامل التمدد الحراري 68-572 | 10.4 · 10-6 per °F (68-572 °F) | 18 · 10-6 per °C (20-300 °C) | |||||||||
| السعة الحرارية محددة | 0.09 وحدة حرارية بريطانية/رطل/درجة فهرنهايت عند 68 درجة فهرنهايت | 377.1 جول/كجم عند 20 درجة مئوية | |||||||||
| معامل المرونة في التوتر | 15200 ksi | 104801 MPa | |||||||||
| الخصائص الفيزيائية التي تقدمها CDA | |||||||||||
خصائص التصنيع
| تقنية | ملاءمة | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| اللحيم | ممتاز | ||||||||||
| مختلط | ممتاز | ||||||||||
| اللحام بالأوكسي أسيتيلين | جيد | ||||||||||
| بقعة اللحام | جيد | ||||||||||
| لحام التماس | جيد | ||||||||||
| بعقب اللحام | جيد | ||||||||||
| القدرة على العمل البارد | مسكين | ||||||||||
| القدرة على التشكيل الساخن | ممتاز | ||||||||||
| تصنيف قابلية التشغيل الآلي | 70 | ||||||||||
| خصائص التصنيع التي تقدمها CDA | |||||||||||
الخصائص الحرارية
| Thermal properties provided by CDATemperature is measured in fahrenheit. **For stress relief, Solution treatment and annealing – time is measured in hours/inch of thickness. For precipitation heat treatment – time is measured in hours. |