C69300 Lead Free Brass
C693 Lead-Free Brass has excellent dezincification corrosion resistance and excellent stress corrosion cracking resistance. One if its unique features is that it is corrosion resistant to chemicals found in water and gas. It has high strength equivalent to stainless steel. It also has good machinability, excellent hot forgeability, easily accepts solder and brazing, and has excellent polishing and plating capabilities. C69300 Lead-Free Brass is compliant with the Federal Drinking Water Act, and it also support applications following the U.S. EPA standards for antimicrobial performance.
Common Applications of C69300 Brass:
السباكة
- Stop Valves
- PEX fittings
- Ball valves
- Commercial and Residential water faucet parts
السيارات
- Fluid Connectors
- Sensor Bodies
- Thermostat Parts
صناعي
- Automatic Screw Machine Parts
- البراغي
- Condenser Tube Plate
- المكسرات
- Pneumatic Fittings
- أجزاء المضخة
- Screw Machine Products
- ينبع الصمام
- Valve Bodies for Water
C69300 Product description:
Compliance: C69300 is compliant with key legislation including (1) Federal Safe Drinking Water Act – SDWA, (2) S. 3874 Federal Reduction of Lead in Drinking Water Act, (3) California AB1953, (4) Vermont Act 193, and is NSF/ANSI/CAN 61-2022 compliant
الاستخدامات النموذجية
Automotive: fluid connectors, sensor bodies, thermostat parts
Industrial: automatic screw machine parts, bolts, condenser tube plate, nuts, pneumatic fittings, pump parts, screw machine parts, valve bodies for water, valve stems
Marine: marine products, propeller shafts
Plumbing: faucet stems, faucets, plumbing fittings, water meter cases
مواصفات مماثلة أو معادلة
| CDA | من | SAE | AMS | الفيدرالية | جيش | آخر |
|---|---|---|---|---|---|---|
| C69300 | B371 B371M |
أدوات معالجة البلاستيك وقوالب الصب بالضغط
| النحاس٪ 1 | الرصاص% | نسبة القصدير | الزنك٪ | الحديد% | ف٪ | Ni%2 | Mn% | و٪ | |||
|---|---|---|---|---|---|---|---|---|---|---|---|
*Pb content is greater than 0.02%. 1Cu value includes Ag. 2Ni value includes Co. Single values represent maximums. | |||||||||||
| 73.00- 77.00 | 0.02*- 0.09 | 0.20 | ريم. | 0.10 | 0.04- 0.15 | 0.10 | 0.10 | 2.70- 3.40 | |||
آلية
| سبائك النحاس رقم UNS. | تصنيف قابلية التشغيل الآلي | الكثافة (رطل/بوصة3 عند 68 درجة فهرنهايت) |
|---|---|---|
| C69300 | 85 | 0.300 |
الخواص الميكانيكية
C69300
H02 half hard
Size range: up to 1/2″ inclusive
| قوة الشد، دقيقة | قوة الخضوع، عند امتداد 0.5% تحت الحمل، دقيقة | Elongation, 4x Diameter or Thickness of Specimen, min | صلابة روكويل "ب". | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | max HRB approx | |
| 85 | 585 | 45 | 310 | 5 | 85 | |
Size range: over 1/2″ to 1″ inclusive
| قوة الشد، دقيقة | قوة الخضوع، عند امتداد 0.5% تحت الحمل، دقيقة | Elongation, 4x Diameter or Thickness of Specimen, min | صلابة روكويل "ب". | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | max HRB approx | |
| 75 | 515 | 35 | 240 | 10 | 80 | |
Size range: over 1″ to 2 1/2″ inclusive
| قوة الشد، دقيقة | Yield strength, at 00.5% extension under load,, min | Elongation, 4x Diameter or Thickness of Specimen, min | صلابة روكويل "ب". | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | max HRB approx | |
| 70 | 480 | 30 | 205 | 10 | 75 | |
الخصائص الفيزيائية
الخصائص الفيزيائية التي تقدمها CDA | |||||||||||
| العادة الأمريكية | قياس | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| نقطة الانصهار - السائل | 1616 °F | 880 °C | |||||||||
| نقطة الانصهار - الصلبة | 1571 °F | 855 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 0.3 lb/in3 at 68 °F | 8.3 gm/cm3 at 20 °C | |||||||||
| جاذبية معينة | 8.3 | 8.3 | |||||||||
| التوصيل الكهربائي | 8% IACS at 68 °F | 0.046 MegaSiemens/cm at 20 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 21.8 Btu/sq ft/ft hr/°F at 68 °F | 37.76 W/m at 20 °C | |||||||||
| Coefficient of thermal expansion 68-212 | 10.3 · 10-6 per °F (68-212 °F) | 17.8 · 10-6 per °C (20-100 °C) | |||||||||
| معامل التمدد الحراري 68-392 | 10.3 · 10-6 per °F (68-392 °F) | 17.8 · 10-6 per °C (20-200 °C) | |||||||||
| معامل التمدد الحراري 68-572 | 10.4 · 10-6 per °F (68-572 °F) | 18 · 10-6 per °C (20-300 °C) | |||||||||
| السعة الحرارية محددة | 0.09 وحدة حرارية بريطانية/رطل/درجة فهرنهايت عند 68 درجة فهرنهايت | 377.1 جول/كجم عند 20 درجة مئوية | |||||||||
| معامل المرونة في التوتر | 15200 ksi | 104801 MPa | |||||||||
خصائص التصنيع
خصائص التصنيع التي تقدمها CDA | |||||||||||
| تقنية | ملاءمة | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| اللحيم | ممتاز | ||||||||||
| مختلط | جيد | ||||||||||
| اللحام بالأوكسي أسيتيلين | جيد | ||||||||||
| لحام القوس المحمي بالغاز | جيد | ||||||||||
| اللحام بالقوس المعدني المطلي | جيد | ||||||||||
| بقعة اللحام | جيد | ||||||||||
| لحام التماس | جيد | ||||||||||
| بعقب اللحام | جيد | ||||||||||
| القدرة على العمل البارد | مسكين | ||||||||||
| القدرة على التشكيل الساخن | ممتاز | ||||||||||
| تقييم النسيان | 95 | ||||||||||
| تصنيف قابلية التشغيل الآلي | 85 | ||||||||||
الخصائص الحرارية
الخصائص الحرارية التي تقدمها CDA * يتم قياس درجة الحرارة بالفهرنهايت. **For stress relief, solution treatment and annealing – time is measured in hours/inch of thickness. For precipitation heat treatment – time is measured in hours. | |||||||||||
| علاج او معاملة | الحد الأدنى* | أقصى* | Value* | Time** | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| تخفيف التوتر | 0 | ||||||||||
| علاج الحل | 0 | ||||||||||
| التلدين | 932 | 1112 | |||||||||
| العلاج الساخن | 1202 | 1517 | |||||||||
عمليات التصنيع المشتركة
Forming and bending, machining, shearing
عمليات التصنيع المشتركة التي تقدمها CDA