C64200, C642 Silicon Aluminum Bronze (AMS 4634)
C64200 Silicon Aluminum Bronze is an engineering alloy at least as resistant to corrosion as copper itself, but much stronger. CDA 642 bronze is manufactured mostly in the form of round, hexagonal, and octagonal rods for hot forming and free machining. C642 is considered to be of the best valve stem alloys. Other applications include gears, marine hardware, nuts, pole line hardware, and valve bodies and components.
- EU Designation: CuAl7Si2, CW302G
- ASTM B150, ASTM B249, QQ-C-465, AMS 4634, SAE J461, SAE J463
Typical Uses for C64200 Silicon Aluminum Bronze:
AUTOMOTIVE: Valve Guides, Automobile Engine
الكهرباء: Pole Line Hardware
مهمات الربط: Bolts, Nuts
صناعي: Valve Components, Valve Bodies, Gears, Valve Stems, Cams
البحرية: Hardware
Aluminum is the main alloying metal added to copper in aluminum bronze alloys such as C64200, also known as C642. A variety of aluminum bronzes of differing compositions have found industrial use, with most ranging from 5.00% to 11.00% aluminum by weight, the remaining mass being copper. Other alloying agents such as iron, nickel, manganese, and silicon are also oftentimes added. Aluminum bronzes are most valued for their high strength and corrosion resistance.
AMS 4634-C64200
Product description: Aluminum bronze
Tempers: HR50 drawn and stress relieved
Solids: 3/16″ to 6″ O.D.
Hex: 1/2″ to 2″ O.D.
Standard lengths: 144″
الاستخدامات النموذجية
Automotive: valve guides (automobile engine)
Electrical: pole line hardware
Fasteners: bolts, nuts
Industrial: cams, gears, valve bodies, valve components, valve stems
Marine: hardware
مواصفات مماثلة أو معادلة
| CDA | من | SAE | AMS | الفيدرالية | جيش | آخر |
|---|---|---|---|---|---|---|
| C64200 | B150 B150M | J461 J463 | 4634 | QQ-C-465 |
أدوات معالجة البلاستيك وقوالب الصب بالضغط
| النحاس٪ 1 | الرصاص% | نسبة القصدير | الزنك٪ | الحديد% | Ni%2 | آل% | Mn% | و٪ | |||
|---|---|---|---|---|---|---|---|---|---|---|---|
1Cu value includes Ag. 2Ni value includes Co. ملحوظة: النحاس + مجموع العناصر المسماة، 99.5% كحد أدنى. تمثل القيم الفردية الحد الأقصى. | |||||||||||
| ريم. | 0.05 | 0.20 | 0.50 | 0.30 | 0.25 | 6.30- 7.60 | 0.10 | 1.50- 2.20 | |||
آلية
| سبائك النحاس رقم UNS. | تصنيف قابلية التشغيل الآلي | الكثافة (رطل/بوصة3 عند 68 درجة فهرنهايت) |
|---|---|---|
| C64200 | 60 | 0.278 |
الخواص الميكانيكية
C64200
HR50 drawn and stress relieved Temper
Size range: up to 1/2″ bars and rods inclusive
| قوة الشد، دقيقة | قوة الخضوع، عند امتداد 0.5% تحت الحمل، دقيقة | Elongation, in 4D, min | Hardness, internal | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB | |
| 90 | 621 | 45 | 310 | 9 | >80 inclusive | |
Size range: 1/2″ to 1″ bars and rods inclusive
| قوة الشد، دقيقة | قوة الخضوع، عند امتداد 0.5% تحت الحمل، دقيقة | Elongation, in 4D, min | Hardness, internal | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB | |
| 85 | 586 | 45 | 310 | 12 | >80 inclusive | |
Size range: over 1″ to 2″ bars and rods inclusive
| قوة الشد، دقيقة | قوة الخضوع، عند امتداد 0.5% تحت الحمل، دقيقة | Elongation, in 4D, min | Hardness, internal | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB | |
| 80 | 552 | 42 | 290 | 12 | >80 inclusive | |
Size range: over 2″ to 3″ bars and rods inclusive
| قوة الشد، دقيقة | قوة الخضوع، عند امتداد 0.5% تحت الحمل، دقيقة | Elongation, in 4D, min | Hardness, internal | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB | |
| 75 | 517 | 35 | 241 | 15 | >80 inclusive | |
الخصائص الفيزيائية
الخصائص الفيزيائية التي تقدمها CDA | |||||||||||
| العادة الأمريكية | قياس | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| نقطة الانصهار - السائل | 1840 °F | 1004 °C | |||||||||
| نقطة الانصهار - الصلبة | 1800 °F | 982 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 0.278 lb/in3 at 68 °F | 7.69 gm/cm3 at 20 °C | |||||||||
| جاذبية معينة | 7.69 | 7.69 | |||||||||
| التوصيل الكهربائي | 8% IACS at 68 °F | 0.047 MegaSiemens/cm at 20 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 26 Btu/sq ft/ft hr/°F at 68 °F | 45 W/m at 20 °C | |||||||||
| معامل التمدد الحراري 68-572 | 10 · 10-6 per °F (68-572 °F) | 17.3 · 10-6 per °C (20-300 °C) | |||||||||
| السعة الحرارية محددة | 0.09 وحدة حرارية بريطانية/رطل/درجة فهرنهايت عند 68 درجة فهرنهايت | 377.1 جول/كجم عند 20 درجة مئوية | |||||||||
| معامل المرونة في التوتر | 16000 كيلو | 110317 ميجا باسكال | |||||||||
| معامل الصلابة | 6000 كيسي | 41369 ميجا باسكال | |||||||||
خصائص التصنيع
خصائص التصنيع التي تقدمها CDA | |||||||||||
| تقنية | ملاءمة | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| اللحيم | لا ينصح | ||||||||||
| مختلط | عدل | ||||||||||
| اللحام بالأوكسي أسيتيلين | لا ينصح | ||||||||||
| لحام القوس المحمي بالغاز | عدل | ||||||||||
| اللحام بالقوس المعدني المطلي | عدل | ||||||||||
| بقعة اللحام | عدل | ||||||||||
| لحام التماس | عدل | ||||||||||
| بعقب اللحام | عدل | ||||||||||
| القدرة على العمل البارد | مسكين | ||||||||||
| القدرة على التشكيل الساخن | ممتاز | ||||||||||
| تقييم النسيان | 80 | ||||||||||
| تصنيف قابلية التشغيل الآلي | 60 | ||||||||||
الخصائص الحرارية
الخصائص الحرارية التي تقدمها CDA * يتم قياس درجة الحرارة بالفهرنهايت. | |||||||||||
| علاج او معاملة | الحد الأدنى* | أقصى* | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| التلدين | 1100 | 1300 | |||||||||
| العلاج الساخن | 1300 | 1600 | |||||||||
عمليات التصنيع المشتركة
Forging, hot forming, machining
عمليات التصنيع المشتركة التي تقدمها CDA