C26000 PRODUCT DESCRIPTION:
Cartridge Brass 70%
TEMPERS: H01 Quarter Hard, H02 Half Hard, H04 Hard
SOLIDS: 3/8″ to 2 1/2″ O.D.
HEX: 3/8″ to 2″ O.D.
STANDARD LENGTHS: 144″
الاستخدامات النموذجية
- ARCHITECTURE: grillwork
- AUTOMOTIVE: electrical connectors, heater cores, odometer contacts, radiator cores, radiator tanks, radiator tube, tanks, thermostats
- BUILDERS HARDWARE: decorative hardware, door knobs, finish hardware, hinges, kick plates, locks, push plates
- CONSUMER: bird cages, buttons, chain links, coinage, costume jewelry, etched articles, fireplace screens, lamps, pen/pencil inserts and clips, planters, shells (electrical sockets), snaps, syringe parts, watch parts
- ELECTRICAL: flashlight shells, lamp fixtures, reflectors, screw shells, terminal connectors
- FASTENERS: eyelets, fasteners, grommets, pins, rivets, screws
- INDUSTRIAL: air pressure conveyer systems, bead chain, chain, heat exchangers, liners, power cylinders, pumps, sound-proofing equipment, springs, tubing for instruments and machines, wire screens
ORDANCE ammunition, ammunition cartridge cases, mechanical housings for lighters, shells (mechanical housings for ammunition) - OTHER: stencils, washers
- PLUMBING: bathroom fixtures, faucet escutcheons, fittings, plumbing accessories, plumbing brass goods, traps
During the manufacturing process of C26000 brass alloy, various sophisticated techniques are employed to ensure the quality and consistency of the alloy. Typically, this alloy is manufactured by electrolysis or vacuum melting, then precisely machined and heated for optimal performance and repeatability.
The strength of C26000 brass alloy is one of the highest among other brass alloys, making it very popular in some applications that require high strength and wear resistance. For example, it is commonly used in the manufacture of mechanical components such as automotive parts, coolers, and joints.
In addition, C26000 brass alloy also has good processability and electrical conductivity properties, which makes it a high-quality material for manufacturing electrical connectors and electronic devices. It is also commonly used to create metal carvings and ornaments because it can be sanded smooth and resistant to paint.
Overall, C26000 Brass Alloy is a high-quality brass alloy that provides excellent performance and durability in a variety of applications. Whether in the mechanical, electronic or decorative fields, C26000 brass alloy is a good choice.
Similar or Equivalent Specification
| CDA | من | SAE | AMS | الفيدرالية | جيش | آخر |
|---|---|---|---|---|---|---|
| C26000 | B927 B927M | J461 J463 | 70/30 |
درجة حرارة التقسية
| النحاس% | الرصاص% | الزنك٪ | الحديد% | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
Chemical Composition according to ASTM B927/B927M-17 Note: Cu + Sum of Named Elements, 99.7% min. Single values represent maximums. | |||||||||||
| 68.50- 71.50 | 0.07 | ريم. | 0.05 | ||||||||
آلية
| Copper Alloy UNS No. | تقييم الماكينة | الكثافة (رطل/بوصة3 عند 68 درجة فهرنهايت) |
|---|---|---|
| C26000 | 30 | 0.308 |
الخصائص الميكانيكية
Mechanical Properties according to ASTM B927/B927M-17
C26000
H01 Quarter Hard
SIZE RANGE: UNDER 1/2″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 50 | 345 | 30 | 205 | 20 | 55 | |
SIZE RANGE: OVER 1/2″ DIAMETER ROD TO 1″ INCLUSIVE
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 48 | 330 | 25 | 170 | 24 | 55 | |
SIZE RANGE: OVER 1″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 46 | 315 | 20 | 140 | 28 | 55 | |
C26000
H02 Half Hard
SIZE RANGE: UNDER 1/2″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 57 | 395 | 35 | 241 | 15 | 70 | |
SIZE RANGE: OVER 1/2″ DIAMETER ROD TO 1″ INCLUSIVE
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 54 | 370 | 32 | 220 | 20 | 70 | |
SIZE RANGE: OVER 1″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 50 | 345 | 30 | 205 | 25 | 70 | |
C26000
H04 Hard
SIZE RANGE: UNDER 1/2″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 70 | 485 | 50 | 345 | 10 | 82 | |
SIZE RANGE: OVER 1/2″ DIAMETER ROD TO 1″ INCLUSIVE
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 65 | 450 | 45 | 310 | 15 | 82 | |
SIZE RANGE: OVER 1″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 60 | 415 | 40 | 275 | 20 | 82 | |
إلى 500 درجة مئوية وتخفيف التوتر
Physical Properties provided by CDA | |||||||||||
| العادة الأمريكية | قياس | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Melting Point – Liquidus | 1750 درجة فهرنهايت | 954 درجة مئوية | |||||||||
| Melting Point – Solidus | 1680 °F | 916 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 0.308 lb/in3 عند 68 درجة فهرنهايت | 8.53 gm/cm3 عند 20 درجة مئوية | |||||||||
| جاذبية معينة | 8.53 | 8.53 | |||||||||
| التوصيل الكهربائي | 28% IACS at 68 °F | 0.162 MegaSiemens/cm at 20 °C | |||||||||
| توصيل حراري | 70 Btu/sq ft/ft hr/°F at 68 °F | 121.2 W/m at 20 °C | |||||||||
| Coefficient of Thermal Expansion 68-572 | 11.1 · 10-6 لكل درجة فهرنهايت (68-572 درجة فهرنهايت) | 19.2 · 10-6 لكل درجة مئوية (20-300 درجة مئوية) | |||||||||
| السعة الحرارية محددة | 0.09 وحدة حرارية بريطانية/رطل/درجة فهرنهايت عند 68 درجة فهرنهايت | 377.1 جول/كجم عند 20 درجة مئوية | |||||||||
| Modulus of Elasticity in Tension | 16000 كيلو | 110317 MPa | |||||||||
| Modulus of Rigidity | 6000 كيسي | 41369 MPa | |||||||||
خصائص التصنيع
Fabrication Properties provided by CDA | |||||||||||
| تقنية | ملاءمة | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| اللحيم | ممتاز | ||||||||||
| مختلط | ممتاز | ||||||||||
| لحام أوكسي أسيتيلين | جيد | ||||||||||
| لحام القوس المحمي بالغاز | جيد | ||||||||||
| لحام القوس المعدني المطلي | لا ينصح | ||||||||||
| بقعة اللحام | عدل | ||||||||||
| لحام التماس | لا ينصح | ||||||||||
| بعقب اللحام | جيد | ||||||||||
| القدرة على العمل البارد | ممتاز | ||||||||||
| القدرة على التشكيل الساخن | عدل | ||||||||||
| تقييم الماكينة | 30 | ||||||||||
الخصائص الحرارية
| علاج او معاملة | الحد الأدنى* | أقصى* | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| التلدين | 800 | 1400 | |||||||||
| المعالجة الساخنة | 1350 | 1550 | |||||||||