C23000 Typical Uses
ARCHITECTURE: etching parts, trim, weather strip
BUILDERS HARDWARE: kick plates
CONSUMER: badges, coinage, compacts, costume jewelry, dials, fire extinguisher cases, lipstick containers, medallions, nameplates, plaques, rouge boxes, tokens, zippers
ELECTRICAL: conduit, rotor bars (AC motors), screw shells, sockets
FASTENERS: eyelets, fasteners
INDUSTRIAL: condensor tubes, fire extinguishers, flexible metal hose, heat exchanger shells, heat exchangers, pickling crates, pump cylinder liners, radiator cores, tags, tubing for heat exchangers, tubing for instrumentation
OTHER fire hose couplings
PLUMBING fittings, j-bends, pipe, pipe nipples, pipe service lines, pump lines, service lines, traps
C23000 brass has high strength, good plasticity, high mechanical properties, and can withstand cold well. Hot pressure processing, welding and corrosion resistance are also good, and it is easy to form.PRODUCT DESCRIPTION: Red Brass 85%
TEMPERS: H01 Quarter Hard, H02 Half Hard, H04 Hard
SOLIDS: 3/8″ to 2 1/2″ O.D.
HEX: 3/8″ to 2″ O.D.
STANDARD LENGTHS: 144″
TEMPERS: H01 Quarter Hard, H02 Half Hard, H04 Hard
SOLIDS: 3/8″ to 2 1/2″ O.D.
HEX: 3/8″ to 2″ O.D.
STANDARD LENGTHS: 144″
Similar or Equivalent Specification
| CDA | من | SAE | AMS | الفيدرالية | جيش | آخر |
|---|---|---|---|---|---|---|
| C23000 | B927 B927M |
درجة حرارة التقسية
| النحاس% | الرصاص% | الزنك٪ | الحديد% | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
Chemical Composition according to ASTM B927/B927M-17 Note: Cu + Sum of Named Elements, 99.8% min. Single values represent maximums. | |||||||||||
| 84.00- 86.00 | 0.05 | ريم. | 0.05 | ||||||||
آلية
| Copper Alloy UNS No. | تقييم الماكينة | الكثافة (رطل/بوصة3 عند 68 درجة فهرنهايت) |
|---|---|---|
| C23000 | 30 | 0.316 |
الخصائص الميكانيكية
Mechanical Properties according to ASTM B927/B927M-17
C23000
H01 Quarter Hard
SIZE RANGE: UNDER 1/2″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 44 | 305 | 20 | 140 | 15 | ||
SIZE RANGE: 1/2″ DIAMETER ROD TO 1″ INCLUSIVE
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 42 | 290 | 17 | 115 | 17 | ||
SIZE RANGE: OVER 1″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 40 | 275 | 15 | 103 | 19 | ||
C23000
H02 Half Hard
SIZE RANGE: UNDER 1/2″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 50 | 345 | 30 | 205 | 7 | 70 | |
SIZE RANGE: 1/2″ DIAMETER ROD TO 1″ INCLUSIVE
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 45 | 310 | 27 | 185 | 10 | 70 | |
SIZE RANGE: OVER 1″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 40 | 275 | 25 | 170 | 12 | 70 | |
C23000
H04 Hard
SIZE RANGE: UNDER 1/2″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 63 | 435 | 40 | 275 | 5 | 82 | |
SIZE RANGE: 1/2″ DIAMETER ROD TO 1″ INCLUSIVE
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 60 | 415 | 37 | 255 | 7 | 82 | |
SIZE RANGE: OVER 1″ DIAMETER ROD
| Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or 4x Thickness, min | Rockwell “B” Hardness | ملاحظات | ||
|---|---|---|---|---|---|---|
| ksi | الآلام والكروب الذهنية | ksi | الآلام والكروب الذهنية | ٪ | HRB نموذجي | |
| 58 | 400 | 35 | 240 | 9 | 82 | |
إلى 500 درجة مئوية وتخفيف التوتر
Physical Properties provided by CDA | |||||||||||
| العادة الأمريكية | قياس | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Melting Point – Liquidus | 1830 درجة فهرنهايت | 999 درجة مئوية | |||||||||
| Melting Point – Solidus | 1770 °F | 966 °C | |||||||||
| سمك 12-300 مم × عرض 200-2300 مم | 0.313 lb/in3 عند 68 درجة فهرنهايت | 8.67 gm/cm3 عند 20 درجة مئوية | |||||||||
| جاذبية معينة | 8.67 | 8.67 | |||||||||
| التوصيل الكهربائي | 32% IACS at 68 °F | 0.186 MegaSiemens/cm at 20 °C | |||||||||
| توصيل حراري | 81 Btu/sq ft/ft hr/°F at 68 °F | 140.3 W/m at 20 °C | |||||||||
| Coefficient of Thermal Expansion 68-572 | 10.6 · 10-6 لكل درجة فهرنهايت (68-572 درجة فهرنهايت) | 18.4 · 10-6 لكل درجة مئوية (20-300 درجة مئوية) | |||||||||
| السعة الحرارية محددة | 0.09 وحدة حرارية بريطانية/رطل/درجة فهرنهايت عند 68 درجة فهرنهايت | 377.1 جول/كجم عند 20 درجة مئوية | |||||||||
| Modulus of Elasticity in Tension | 16000 كيلو | 110317 MPa | |||||||||
| Modulus of Rigidity | 6000 كيسي | 41369 MPa | |||||||||
خصائص التصنيع
Fabrication Properties provided by CDA | |||||||||||
| تقنية | ملاءمة | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| اللحيم | ممتاز | ||||||||||
| مختلط | ممتاز | ||||||||||
| لحام أوكسي أسيتيلين | جيد | ||||||||||
| لحام القوس المحمي بالغاز | جيد | ||||||||||
| لحام القوس المعدني المطلي | لا ينصح | ||||||||||
| بقعة اللحام | عدل | ||||||||||
| لحام التماس | لا ينصح | ||||||||||
| بعقب اللحام | جيد | ||||||||||
| القدرة على العمل البارد | ممتاز | ||||||||||
| القدرة على التشكيل الساخن | جيد | ||||||||||
| تقييم الماكينة | 30 | ||||||||||
الخصائص الحرارية
Thermal Properties provided by CDA * يتم قياس درجة الحرارة بالفهرنهايت. | |||||||||||
| علاج او معاملة | الحد الأدنى* | أقصى* | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| التلدين | 800 | 1350 | |||||||||
| المعالجة الساخنة | 1450 | 1650 | |||||||||
Common Fabrication ProcessesBlanking, Coining, Drawing, Etching, Forming and Bending, Heading and Upsetting, Piercing and Punching, Roll Threading and Knurling, Shearing, Spinning, Squeezing and Swaging, Stamping
Common Fabrication Processes provided by CDA